牌号简介 About |
---|
双组分聚氨酯树脂通用型树脂(防水型),由于双组分树脂的分子量很低,需要添加和混合足够的交联剂。增加分子量,使聚氨酯分子结构更加网状,从而提高膜的强度。适用于纱线固定、底漆涂层、毛孔填充。高固含量可提高织物涂层的耐水压性、毛重和牢固感。添加促进剂可改善老化条件,增强粘附力。布层压。布料和TPU&PVC层压。直接涂层。耐水性高,不发黄,耐水湿,手感好,剥离强度好。直接涂层用聚氨酯树脂。适用于打底。 Two component PU Resins General type resin (waterproof) Because the molecular weight of two componet resin is quite low, adding and mixing adequate crosslinker is necessary. It would increase molecular weight and make more meshed PU structure, which would enhance the strength of membrane. Applied to yarn fixation, primer coating, pore filling. The high solid content would enhance water pressure resistance, gross, and firm-feeling of textile coating. Adding promotors would enhance aging condition and reinforce adhesion. Cloth lamination. Lamination of cloth and TPU&PVC. For direct coatings. High water resistance, non-yellowing, hydrosis resistance, good hand-feel, good peeling strength. PU resin for direct coating. Applied to bottoming. |
技术参数 Technical Data | |||
---|---|---|---|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
溶剂 solvent |
DMF/TOL | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
Clear/Yellow Tint | ||
固体含量 Solid content |
44 到 46 | % | |
粘度 viscosity |
|||
25℃ 25℃ |
30 到 60 | Pa·s | |
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
100% 正割 100% secant |
0.981 到 1.96 | MPa | |
拉伸强度 tensile strength |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
科莱恩与INDIA GLYCOLS建立可再生环氧乙烷衍生物合资企业
2021-07-02 搜料网资讯: 2021年7月1日,科莱恩宣布与印度乙二醇有限公司(IGL)创建可再生环氧乙烷(EO)衍生物合资企业。该合资企业将以科莱恩IGL特种化学品私人有限公司的名义运营。 科莱恩首席执 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |