牌号简介 About |
---|
特点:高熔体流动速率均聚聚丙烯,具有高刚度、易充型、含核添加剂等特点。推荐用途:薄壁刚性容器注射成型,周期快,通用注射成型应用。 Characteristics: High melt flow rate Homopolymer polypropylene with high stiffness and easy mold filling, with nucleant additive. Recommended for: Injection molding of thin wall rigid containers, fast cycle time, general purpose injection molding applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate 2 |
|||
230℃,2.16kg 230℃,2.16kg 2 |
22 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 3 |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding 3 |
38.6 | MPa | ASTM D638 |
拉伸应变 Tensile strain 3 |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding 3 |
6.5 | % | ASTM D638 |
弯曲模量 Bending modulus 4 |
|||
1% 正割,3.20 mm,注塑成型 1% cut, 3.20 mm, injection molded 4 |
1930 | MPa | ASTM D790-A |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm,注塑成型 23 ℃, 3.2mm, injection molding |
32 | J/m | ASTM D256-A |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 程序 B |
3 类型 1, 2,0 in/min |
4 类型 1, 0,051 in/min |
【新闻资讯】查看全部
康达新材拟1750万元增资聚发新材
2021-01-02 搜料网资讯: 12月30日,康达新材发布公告称,公司与成源、鞠明杰、邓军发、李承帅(合称交易对方)等人于2020年12月30日在上海市签署了《关于南京聚发新材料有限公司之增资协议》(以 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |