牌号简介 About |
---|
ES-215系列高温表面涂层的研制是为了满足飞机和航空航天工业对170°C/350°F以上高温应用的要求。这些表面涂层已在试验中证明,它们与预浸系统的相容性可产生在热和真空条件下固化的良好表面条件。M套袋。在模具和复合材料制造中,这些系统的热循环表现出高度的物理稳定性。这些系统是通用的,因为它们可以用于RHL和IHL热环境应用。这些质量允许制造商使用一个单一的系统,该系统将保持两种规格,而不是使用两种不同的系统。这些系统在卫生上对车间使用是安全的,因为它们不包含MDA或VCHD。与任何ADTech高温层压树脂一起使用。 ES-215 SERIES HIGH-TEMP SURFACE COATS were developed to meet the requirements of the aircraft and aerospace industry for use which demands higher temperature applications greater than 170°C/350°F. These surface coats have proven in tests that their compatibility with prepreg systems produce excellent surface conditions cured under heat and vacuum bagging. The thermo-cycling of these systems exhibit a great degree of high physical stability when used in tooling and composite fabrication. These systems are versatile in that they can be used in RHL and IHL heat environment applications. These qualities allow the fabricator a single system which will sustain both specifications in deference to using two different systems. These systems are hygienically safe for shop usage as they do not contain MDA OR VCHD. Use in conjunction with any ADTECH high-temp laminating resin. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表观密度 Apparent density |
1.23 | g/cm³ | ASTM D1895 |
吸水率 Water absorption rate |
0.16 | % | ASTM D570 |
粘度 viscosity |
|||
固化剂 curing agent |
0.05 到 0.06 | Pa·s | |
树脂,25℃ Resin, 25 ℃ |
Thixotropic | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
190 | J/m | ASTM D256 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
工作期限 Working period |
hr | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
断裂 fracture |
MPa | ASTM D790 | |
压缩强度 compressive strength |
|||
Ultimate Ultimate |
MPa | ASTM D965 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
贮藏期限 Storage period |
|||
-- -- 2 |
wk | ||
-- -- 3 |
wk | ||
热固性混合粘度 Thermosetting mixed viscosity |
|||
25℃ 25℃ |
cP | ASTM D2393 | |
脱模时间 stripping time |
min | ||
Tack Free Time Tack Free Time |
hr |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Resin in original nopened container |
3 Hardener in original nopened container |
【新闻资讯】查看全部
赢创和Samaplast合作提升聚醚醚酮(PEEK)植入物性能
2021-10-08 搜料网资讯: 特种化学品公司赢创与瑞士高性能聚合物注塑专业公司Samaplast展开合作,成功通过注塑成型工艺生产出基于骨传导性聚醚醚酮(PEEK)材料的脊柱植入物原型。这一成果整合 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |