牌号简介 About |
---|
应用:用于生产玻璃、碳纤维或芳纶纤维增强的层压段,使用:飞机零件、帆船、运动船、车身……特殊性能:无填充材料的极液体低分子树脂类型:低分子环氧层压树脂应用方法:根据应用方法和要求的层压板最终性能,将Letoxit Pr 220与合适的固化剂混合。从生产5米开始,可以使用Letoxit EM 315、EM 316或EM 317。如果未规定混合比,则可以确定100g环氧树脂的固化剂数量(单位:克):x=He。eekv x=100克环氧树脂的固化剂数量(单位:克):he=固化剂的氢当量重量eekv=环氧树脂当量(单位:摩尔/100克) Applications: for production of laminated segments reinforced with glass, carbon or kevlar fibers using: parts of airplanes, sailplanes, sport boats, carriage bodies…. Special properties: extremely liquid low molecular resin without filling material Type: low molecular epoxy laminated resin Application method: Mix Letoxit PR 220 with suitable curing agent according to the application method and required final properties of laminates. From production of 5M it is possible to use Letoxit EM 315, EM 316 or EM 317. If the mixture ratio is not stated, it is possible to determine the quantity of curing agent in grams for 100g of epoxy resin: x = He . Eekv x = quantity of curing agent in grams for 100 grams of epoxy resin resin: He = hydrogen equivalent weight of curing agent Eekv = epoxy equivalent epoxy resin in mol/100 g |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.15 到 1.23 | g/cm³ | |
溶液粘度 Solution viscosity 2 |
600 到 900 | mPa·s | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
贮藏期限 Storage period |
26 | wk | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
环氧当量 Epoxy equivalent |
E(evk | ||
Storage Temperature Storage Temperature |
5 到 35 | ℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 25°C |