符合ISO 1043-1的化学缩写:POM-Hi,成型化合物ISO 9988-POM-K,M-GNPR,05-001 POM共聚物,基于HOSTAFORM C 27021的改性易流动弹性体,含有注射成型类型;冲击强度高,硬度、刚度和耐化学性略低于基本类型;耐热性高。l和氧化降解。UL自然注册,厚度超过1.57 mm,符合UL 94 HB。厚度大于1 mm时,燃烧速率为ISO 3795和FMVSS 302<100 mm/min。应用范围:对于具有更高能量吸收能力的薄壁模塑件,ul=保险商实验室(美国)fmvss=联邦机动车辆安全标准(美国) Chemical abbreviation according to ISO 1043-1: POM-HI, Molding compound ISO 9988- POM-K, M-GNPR, 05-001 POM copolymer, modified Easy flowing elastomer-containing injection molding type based on HOSTAFORM C 27021; with higher impact strength and slightly lower hardness, rigidity and chemical resistance than the basic type; high resistance to thermal and oxidative degradation. UL-registration in natural and a thickness more than 1.57 mm as UL 94 HB. Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm thickness. Ranges of applications: For thin-walled molded parts with higher energy-absorbing capacity UL = Underwriters Laboratories (USA) FMVSS = Federal Motor Vehicle Safety Standard (USA) |
产品描述 Product Description
厂家:美国塞拉尼斯 Celanese
类别:POM共聚 Copolymer Polyformaldehyde
用途:薄壁部件;
加工条件:注射成型 Injection Molding
性能特点: 防火阻燃等级HB; 冲击性能好; 易流动; 韧性好; Good flexibility,High impact resistance,Good liquidity,HB
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.39 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
190℃,2.16 kg 190℃,2.16 kg |
20.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
1.8 | % | ISO 294-4 |
MD MD |
1.9 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
0.65 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/1A/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2/1A/50 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
% | ISO 527-2/1A/50 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10°C/min |
【新闻资讯】查看全部
天然双层石墨烯中发现新量子效应!
2022-08-23 扫描上图二维码,可以免费下载 搜料 APP 德国哥廷根大学领导的一个国际研究团队在最新一期《自然》杂志上发表了一篇论文,称他们在对天然双层石墨烯的高精度研究中发现了新的量 |
天然双层石墨烯中发现新量子效应!
扫描上图二维码,可以免费下载搜料APP
德国哥廷根大学领导的一个国际研究团队在最新一期《自然》杂志上发表了一篇论文,称他们在对天然双层石墨烯的高精度研究中发现了新的量子效应,并从理论上解释了这些效应。该系统制备简单,为载荷子和不同相之间的相互作用提供了新的见解,有助于理解所涉及的过程,并促进了量子计算机的发展。 2004年,两位英国科学家使用一种非常简单的实验方法从石墨上剥离石墨片,并在一条特殊胶带的帮助下获得了仅由一层碳原子组成的石墨烯。石墨烯是强度最高的材料之一。它具有良好的韧性、超导热性和导电性,具有广阔的应用前景。如果两层石墨烯以特定角度偏转,所得系统甚至会表现出超导性和其他激发量子效应,如磁性。但到目前为止,制备这种偏转双层石墨烯是困难的。 进一步发现,石墨烯中的电子可以在略高于绝对零度(-273.15℃)的温度下相互作用,并出现各种意想不到的复杂量子相。如果相互作用导致电子自旋对齐,则材料在没有外部影响的情况下具有磁性。通过改变电场,研究人员还可以不断改变双层石墨烯中载流子相互作用的强度。此外,电子运动的自由度在一定条件下会受到限制,形成电子晶格,并且由于相互排斥,它不再有利于电荷的传输,导致系统的电绝缘。 哥廷根大学物理系的托马斯·韦茨教授说,新系统的主要优点之一就是材料制备非常简单,不需要像以前那样,研究人员必须在高温下才能获得所需的结果。该系统可以用于进一步研究各种量子态和量子计算机。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- 奥迪刹车灯框
- 2019-07-31 0
- Hostaform POM共聚物非常坚硬和僵硬,是奥迪A4中的第三个制动灯就是目前使用的Xap级hostaform车辆。由于其暴露在后窗后面,因此软管式XAP部件必须具有良好的紫外线稳定性。另外一个问题是温度的
- 阅读全文
奥迪刹车灯框
奥迪A4中的第三个制动灯就是目前使用的Xap级hostaform车辆。由于其暴露在后窗后面,因此软管式XAP部件必须具有良好的紫外线稳定性。另外一个问题是温度的极端差异,这反过来需要良好的热变形阻力和抗冻性。制动灯的颜色必须与车辆的颜色匹配。
收起
- 氙气灯清洗喷嘴活塞和外壳
- 2019-01-25 0
- Hostaform® S 27063为注塑成型的POM共聚物,流动性能优良
- 阅读全文
氙气灯清洗喷嘴活塞和外壳
1-具有出色的流动性能,优良的加工性
2-具有极低的吸水率,耐水解性能好
3-具有优异的弯曲模量,机械性能好
4-抗冲击强度高,耐冲击性能好
5-具有良好的刚性,高柔韧性
6-非常好的耐摩擦和磨损性能
7-耐候性好,抗紫外线辐射能力强
2-具有极低的吸水率,耐水解性能好
3-具有优异的弯曲模量,机械性能好
4-抗冲击强度高,耐冲击性能好
5-具有良好的刚性,高柔韧性
6-非常好的耐摩擦和磨损性能
7-耐候性好,抗紫外线辐射能力强