牌号简介 About |
---|
NGL015FG是IEPL利用加拿大杜邦的“SCLARTECH”溶液聚合工艺生产的一种基于丁烯共聚单体的低密度聚乙烯树脂(现为Nova Chemicals),它提供了无滑脱和抗阻添加剂的窄分子量分布共聚物,专为生产高强度B而设计。多层膜、气泡膜和层压膜用各种厚度的低膜。 NGL015FG is a Butene Co-monomer based Liner Low Density Polyethylene Resin manufactured by IEPL using "SCLAIRTECH" solution polymerisation process of DU Pont, Canada (Now Nova Chemicals) offers narrow molecular weight distribution copolymer without slip & antiblock additive which has been specifically designed for the production of high strength blown film of various thickness for multilayer, air bubble film & lamination film application. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.919 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.5 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
12.5 | MPa | ASTM D882 |
TD,屈服 TD, yield |
12.0 | MPa | ASTM D882 |
MD,断裂 MD, fracture |
30.0 | MPa | ASTM D882 |
TD,断裂 TD, fracture |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
落锤冲击 Drop hammer impact |
kN/m | ASTM D1709 | |
撕裂强度 tear strength |
ASTM D1922 | ||
MD MD |
kN/m | ASTM D1922 | |
TD TD |
kN/m | ASTM D1922 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
合理的模具构造设计打造最佳的模具功能
2016-07-22 良好的铸件结构设计,铸件壁厚尽可能均匀,避免产生热节,以减少模具局部热量集中产生的热疲劳。铸件的转角处应有适当的铸造圆角,以避免模具上有尖角位导致应力产生。 合理的模具结构设计 1)模具中各元件应有足够的刚度、强度,以承受压力而不变形。模具壁厚要足够,才能减少变形。 2)浇注系统设计尽量减少对型芯冲击、冲蚀。 3)正确选择各元件的公差配合和表面粗糙度。 4)保持模具热平衡。 3.规范热处理工艺< |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |