牌号简介 About |
---|
聚甲醛共聚物,改性注射成型型,含弹性体;具有较高的冲击强度和略低的硬度、刚度和耐化学性,比基本型软管C 9021降低了排放等级,排放符合VDA 275<5 mg/kg的良好焊接强度。根据FMVSS 302的燃烧速度<100 mm/min(1 mm厚)初步数据表 POM copolymer, modified Injection molding type, elastomer-containing; with higher impact strength and slightly lower hardness, rigidity and chemical resistance than the basic type HOSTAFORM C 9021 Reduced emission grade, Emission according to VDA 275 < 5 mg/kg good weld strength. Burning rate according to FMVSS 302 < 100 mm/min (1 mm thickness) Preliminary Datasheet |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.33 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
190℃,2.16 kg 190℃,2.16 kg |
4.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
1.8 | % | ISO 294-4 |
MD MD |
1.9 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
1.0 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/1A/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2/1A/50 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
% | ISO 527-2/1A/50 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃,局部断裂 -30 ℃, localized fracture |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
ISO 179/1eU | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10°C/min |
【新闻资讯】查看全部
Indorama收购Invista Resins & Fibers G
2019-01-02 Indorama风险投资公众有限公司 (Indorama Ventures Public Co. Ltd.,IVL)宣布,正在收购Invista旗下的PET制造商Invista Resins & Fibers G |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |