牌号简介 About |
---|
Lytex 4142是一种环氧树脂基编织玻璃纤维增强片材成型化合物。玻璃钢筋为1581型0-90双轴玻璃布。建议在需要机织物的应用中使用。Lytex 4142可以使用常规设备和快速循环进行压缩成型。 Lytex 4142 is an epoxy matrix, woven glass fiber reinforced sheet molding compound. The glass reinforcement is 1581 style 0-90 biaxial glass cloth. Its use is suggested for applications where a woven fabric is desirable. Lytex 4142 can be compression molded using conventional equipment and fast cycles. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.95 | g/cm³ | ASTM D792 |
表观密度 Apparent density |
1.94 | g/cm³ | ASTM D1895 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.080 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
379 | MPa | ASTM D638 |
弯曲模量 Bending modulus |
22800 | MPa | ASTM D790 |
弯曲强度 bending strength |
MPa | ASTM D790 | |
压缩模量 Compression modulus |
MPa | ASTM D695 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脱模时间 stripping time |
|||
138℃ 138℃ |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
100%可回收!科学家发明新材料聚二酮烯胺,未来将天下无毒?
2022-05-13 人类赖以生存和发展的环境正在遭到前所未有的破坏,全球变暖、臭氧层耗竭等一系列严重影响人类健康与生存的全球性危机正威胁着每一位现代人。我们的地球正面临一场前所未有的 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |