牌号简介 About |
---|
SABIC® LDPE 2101N0W是一种具有良好韧性和双轴收缩性能的牌号。该材料不含添加剂,在加工过程中能耗低,且具有良好的拉伸性能。应用SABIC® LDPE 2101N0W通常用于薄膜收缩。由于迁移水平非常低,SABIC® LDPE 2101N0W通常可用于食品应用。本产品不适用于任何医药/医疗应用,也不得用于任何医药/医疗应用。 SABIC® LDPE 2101N0W is a grade with good toughness and biaxial shrink properties. The material contains no additives, has a low energy consumption during processing and a good draw down ability. Application SABIC® LDPE 2101N0W is typically used for thin shrink film. SABIC® LDPE 2101N0W can typically be used for food applications due to very low migration levels. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.921 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.85 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
吹塑薄膜 Blown film |
1.0 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
50 | µm | |
拉伸模量 Tensile modulus |
ISO 527-3 | ||
MD,50 µm,吹塑薄膜 MD, 50 µ m, blow molded film |
170 | MPa | |
TD,50 µm,吹塑薄膜 TD, 50 µ m, blow molded film |
MPa | ||
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,50 µm,吹塑薄膜 MD, yield, 50 µ m, blow molded film |
MPa | ||
TD,屈服,50 µm,吹塑薄膜 TD, yield, 50 µ m, blow molded film |
MPa | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ||
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ||
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ||
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁冲击强度 Izod notched impact strength |
|||
50µm,吹塑成型 50 µ m, blow molded |
J/cm | ASTM D4272 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003A | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻塞力 Blocking force |
|||
吹塑薄膜,50.0 µm Blow molded film, 50.0 µ m |
g | 内部方法 | |
Re-blocking - 吹塑薄膜(50.0 µm) Re blocking - blow molded film (50.0 µ m) |
g | 内部方法 | |
撕裂强度 tear strength 1 |
ISO 6383-2 | ||
MD,50 µm MD,50 µm |
kN/m | ||
TD,50 µm TD,50 µm |
kN/m | ||
memo_intro memo_intro |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Blown Film |
【新闻资讯】查看全部
美国总统拜登发表上任后首份外交政策演讲
2021-02-10 搜料网资讯: 当地时间4日下午14时45分(北京时间5日3时45分),美国总统拜登在会见国务院官员后,发表了上任后的首份外交政策演讲,在近20分钟时间里,拜登首先强调:美国回来了 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |