牌号简介 About |
---|
isplen PC270BS是一种含20%矿物填料和中等熔体流动速率的均聚物化合物。具有高刚度、低翘曲收缩性能、良好的美学性能和高光泽表面。应用美观的应用,需要良好的光泽表面。卫生用品。背胶钩环紧固件。家用电器。推荐的熔化温度范围为190至250°C。应优化每个生产线的加工条件。 ISPLEN® PC270BS is a homopolymer compound charged with 20% mineral fillers and medium melt flow rate. It shows high stiffness, low warpage and shrinkage behaviour, good aesthetic properties and high gloss surface. APPLICATIONS Aesthetic applications which require good gloss surface. Hygienic product. Adhesive backed hook and loop fasteners. Electrodomestical appliances. Recommended melt temperature range from 190 to 250°C. Processing conditions should be optimised for each production line. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
12 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
1.0 | % | ISO 294-4 |
MD MD |
0.90 | % | ISO 294-4 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
1850 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
-20℃ -20℃ |
kJ/m² | ISO 179 | |
0℃ 0℃ |
kJ/m² | ISO 179 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ISO 306/A120 | |
B120 B120 |
℃ | ISO 306/B120 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
优化后的巴斯夫TPU是制造鞋支撑片的理想选择
2018-08-08 优化后的巴斯夫热塑性聚氨酯弹性体(TPU)具备卓越的机械性能,是制造鞋支撑片的理想选择 创新材料技术帮助提高鞋履装饰部件的设计自由度 高能效TPU品级最大可将生产周期缩短30 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |