牌号简介 About |
---|
Styrolux® 656C是一种透明的丁苯共聚物(SBC),具有增强的流动性能。它几乎专门用于需要最高清晰度和表面光泽的刚性、坚硬零件的注塑成型。Styrolux® 656C可通过伽马射线灭菌,具有良好的铰链性能。特点:坚固耐用,提高流动性,高清晰度,符合法规要求的应用,塑料容器和瓶子,玩具,显示器,电器外壳,医疗设备 Styrolux® 656C is a clear styrene-butadiene copolymer (SBC) with enhanced flow properties. It is used almost exclusively for injection molding of rigid, tough parts requiring highest levels of clarity and surface gloss. Styrolux® 656C is sterilizable by gamma-rays and offers good hinge properties. FEATURES Tough and stiff grade Enhanced flowability High clarity Regulatory compliant APPLICATIONS Moulded containers and bottles Toys Displays Appliance housings Medical devices |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.02 | g/cm³ | ASTM D792 |
密度 Density |
1.02 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
15 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
200℃,5 kg 200℃,5 kg |
16.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
0.30 to 1.0 | % | ISO 294-4 |
MD MD |
% | ASTM D955 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ASTM D570 | |
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
5% 应变 5% strain |
MPa | ||
-- -- |
MPa | ISO 178 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
MD,断裂 MD, fracture |
% | ISO 527-3 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-A | |
23℃ 23℃ |
kJ/m² | ISO 180-A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
Peak force Peak force |
J | ASTM D3763 | |
Total energy Total energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed 2 |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,退火 0.45 MPa, annealed 2 |
℃ | ISO 75-2/B | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 3 | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
MD MD |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电常数 Dielectric constant |
|||
100 Hz 100 Hz |
IEC 60250 | ||
1.00 mm,1 MHz 1.00 mm,1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index 4 |
ASTM D542 | ||
折射率 Refractive index |
ISO 489 | ||
透光率 Transmittance |
|||
550 nm 550 nm |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 4h/80°C |
3 标准 B (120°C/h), 压 力1 (10N) |
4 Sodium D Line |
【新闻资讯】查看全部
亚洲深水导管架海上安装纪录刷新
2022-04-13 4月11日,由天津港保税区企业海洋石油工程股份有限公司(以下简称海油工程)负责EPCI(设计、采购、建造、安装)总承包的亚洲第一深水导管架海基一号在南海东部珠江口盆地海域成功滑 |
亚洲深水导管架海上安装纪录刷新 4月11日,由天津港保税区企业海洋石油工程股份有限公司(以下简称“海油工程”)负责EPCI(设计、采购、建造、安装)总承包的亚洲第一深水导管架“海基一号”在南海东部珠江口盆地海域成功滑移下水并精准就位。这是国内首次在近300米水深海域安装固定式导管架,也创造了亚洲深水导管架海上安装新纪录。 “海基一号”总高度达302米,总重达3万吨,所用钢材可制造1艘中型航空母舰。“‘海基一号’是按照百年一遇的恶劣海况进行设计,项目团队攻克南海超强内波流、海底巨型沙波沙脊、万吨级环境荷载、超大型结构物精准下水就位等一系列世界性难题,创新应用深水导管架浮动式下水桁架、超大尺寸X撑结构、封舱隔板设计、大尺度大吨位结构多台吊机联合吊装、适应沙坡沙脊的防沉板方案、数字孪生等10余项新技术,实现深水导管架设计建造技术从基础理论、结构型式、设计理念、施工工艺到运行维护等的全方位提升。” 海油工程陆丰油田群区域开发工程总包项目经理阳连丰说。 由于“海基一号”吨位超过世界最大浮式起重船的吊装能力,因此本次海上安装采用滑移下水方式进行,即利用导管架自身重力并配合液压千斤顶助推,使导管架从驳船平稳地滑入海中,再通过起重船将导管架吊装扶正坐底,从而实现安装就位。据中国海油工程建设部副总经理刘义勇介绍,为保证安装顺利进行,中国海油调配国内优势资源,投入亚洲最大下水驳船“海洋石油229”、亚洲第二单吊起重船“蓝鲸”号等亚洲顶级海洋工程船舶,首创“三主作业船”联合施工模式,创新应用“运输监测系统”和“下水运动监测系统”,攻克带压注水、水下灌浆等多项技术难题,经过50余个小时的连续作业,成功实现了精准安装。 据了解,“海基一号”是我国首次尝试300米级深水导管架平台开发模式,与以往类似深水油气田常用的“水下生产系统+浮式生产平台”开发模式相比,更具经济性与安全性,可大幅降低钻完井、工程以及后续的生产操作成本。该模式的成功应用为经济有效开发我国200米至400米水深海域油气资源开拓了一条新的道路。 未来,“海基一号”将服役于我国陆丰油田群区域开发项目陆丰15-1油田。该油田投产后高峰年产原油量将达185万吨。后续,海油工程将进行平台上部组块的安装、调试作业。平台整体建成后,将刷新我国海上原油生产平台的重量纪录。
图为“海基一号”下水现场 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。