牌号简介 About |
---|
Solef® 1006聚偏氟乙烯是一种非常低粘度的均聚物树脂,主要用于注塑或复丝挤出。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.75 to 1.80 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
30 to 40 | g/10min | ASTM D1238 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
< 0.040 | % | ASTM D570 |
收缩率 Shrinkage rate |
|||
Linear Linear |
2.0 to 3.0 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,1 秒,2.00 mm Shore D, 1 second, 2.00 mm |
73 to 80 | ASTM D2240 | |
拉伸模量 Tensile modulus 2 , 3 |
|||
23℃,2 mm 23℃,2 mm 2 , 3 |
MPa | ASTM D638 | |
拉伸强度 tensile strength 4 |
|||
断裂,23℃,2 mm Fracture, 23 ℃, 2 mm 4 |
MPa | ASTM D638 | |
屈服,23℃,2 mm Yield, 23 ℃, 2 mm 4 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 4 |
|||
断裂,23℃,2 mm Fracture, 23 ℃, 2 mm 4 |
% | ASTM D638 | |
屈服,23℃,2 mm Yield, 23 ℃, 2 mm 4 |
% | ASTM D638 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,CS-10 转轮 1000 cycles, 1000 g, CS-10 wheels |
mg | ASTM D4060 | |
摩擦系数 friction coefficient |
ASTM D1894 | ||
动态 dynamic |
ASTM D1894 | ||
静态 static state |
ASTM D1894 | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃,4mm,2m/s 23℃,4mm,2m/s |
J/m | ASTM D6110 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D4065 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 5 | |
熔融温度 Melting temperature |
℃ | ASTM D3418 | |
结晶峰温度 Crystallization peak temperature 12 |
|||
DSC DSC 12 |
℃ | ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:0~40℃ MD:0~40℃ |
1/℃ | ASTM D696 | |
比热 specific heat |
ASTM E968 | ||
23℃ 23℃ |
J/kg/℃ | ASTM E968 | |
100℃ 100℃ |
J/kg/℃ | ASTM E968 | |
导热系数 Thermal conductivity coefficient |
|||
23℃ 23℃ |
W/m/K | ASTM C177 | |
结晶热 Crystallization heat |
J/g | ASTM D3417 | |
结晶点 Crystallization point |
℃ | ASTM D3418 | |
融合热量 Fusion heat |
J/g | ASTM D3417 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
23℃ 23℃ |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
23 ℃,1.0 mm,1 kHz 23 ℃,1.0 mm,1 kHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.10 mm 0.10 mm |
UL 94 | ||
Oxygen Index(3.00 mm) Oxygen Index(3.00 mm) 6 |
% | ASTM D2863 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 4, 0.039 in/min |
3 试样制备方法显著影响其机械性能 |
4 类型 4, 2.0 in/min |
5 速率 A (50°C/h), 载荷2 (50N) |
6 片材 |
【新闻资讯】查看全部
中国对再生塑料的出口禁令即国门利剑
2018-05-15 中国对再生塑料的进口禁令即国门利剑,将更深地刺痛世界各地的回收商。 世界上人口最多的国家中国,在继去年不再接受消费后废料的决策之后,现正推出一项工业废料禁令。 国门利剑是个涉及广泛的项目, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |