牌号简介 About |
---|
KER® 1789是一种充油丁苯橡胶。以松香和脂肪酸皂为原料,采用冷乳液共聚工艺生产,含40.0%化学键合苯乙烯。它通过酸和合成混凝剂系统进行混凝,含有27%(37.5 phr)的扩张油,多环芳烃(RAE级)含量降低,并通过染色抗氧化剂进行稳定。应用KER® 1789适用于生产轮胎(包括轮胎再胎面)和各种技术橡胶制品的橡胶化合物。未批准生产与食品或饮用水接触的橡胶制品。 KER® 1789 is a grade of oil extended styrene-butadiene rubber. It is produced by a technology of cold emulsion copolymerization based on soaps of rosin and fatty acids and contains 40.0% of chemically bonded styrene. It is coagulated by a system of acid and synthetic coagulant, contains 27% (37.5 PHR) of extender oil with reduced content of polycyclic aromatics (RAE grade) and is stabilized by a staining antioxidant. APPLICATION KER® 1789 is appropriate for rubber compounds used for production of tyres including tyre re-treading, and various technical rubber articles. It is not approved for production of rubber articles coming into contact with food or drinking water. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
门尼粘度 Mooney viscosity |
|||
ML 1+4,100℃ ML 1+4,100℃ |
50 到 60 | MU | ASTM D1646 |
结合苯乙烯 Combined with styrene |
38.5 到 41.5 | % | ASTM D5775 |
含油量 oil content |
25 到 29 | wt% | ASTM D5774 |
Organic Acid Organic Acid |
4.0 到 6.0 | wt% | ASTM D5774 |
Soap Soap |
< 0.4 | wt% | ASTM D5774 |
灰份含量 Ash Content |
% | ASTM D5667 | |
挥发物 Volatiles |
wt% | ASTM D5668 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
科思创弹性体用于中国海底电缆
2016-06-30 未来三至五年,市场容量预计增加到1万兆瓦。一旦成行,中国的OWF在市场容量及产量上会成为世界最大的市场之一,超过欧洲现有的以及筹备中的全部产能。 两家公司合作开发电缆保护系统(CPS),保护易受海浪和潮汐侵袭地带的贵重且脆弱的海底电缆。开发的防护手段包括弯曲加强剂和弯曲限定器。大部分的技术手段都隶属Tekmar应用科思创特殊弹性体材料开发的TEKLINK® CPS系统。 TEKLINK® CPS是线缆连接及防护的专利型CPS系统。产品包括阻尼运动加强剂以及可 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |