Lexan Lux7436C树脂Lexan Lux7436C聚碳酸酯(PC)树脂是一种非填充、注射成型级树脂。这种非氯化、非溴化阻燃PC的UL-94V0额定值为1.2 mm/5VA额定值为3.0 mm,并且紫外线稳定(F1额定值)提供了额外的耐候性。Lexan Lux7436C提供扩散色。 LEXAN LUX7436C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.2 mm / 5VA rating at 3.0mm and is UV stabilized(F1 rating) providing additional weathering capability. LEXAN LUX7436C is available in diffusion colors. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.19 | g/cm³ | ASTM D792 |
密度 Density |
1.20 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
10 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
9.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD:3.2 mm TD:3.2 mm |
0.60 to 0.80 | % | 内部方法 |
MD:3.2 mm MD:3.2 mm |
% | 内部方法 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
耐候性 Weathering resistance |
UL 746C | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength 3 |
|||
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
屈服 yield |
MPa | ISO 527-2/50 | |
屈服 yield 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture |
% | ISO 527-2/50 | |
断裂 fracture 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
屈服 yield 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
|||
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 7 |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 8 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D4812 | ||
-30℃ -30℃ |
ASTM D4812 | ||
23℃ 23℃ |
ASTM D4812 | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 8 |
ISO 180/1U | ||
-30℃ -30℃ |
ISO 180/1U | ||
23℃ 23℃ |
ISO 180/1U | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 9 |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,100 mm跨距 1.8 MPa, unannealed, 100 mm span 9 |
℃ | ISO 75-2/Ae | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,100 mm跨距 0.45 MPa, unannealed, 100 mm span 9 |
℃ | ISO 75-2/Be | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 10 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~80℃ TD:23~80℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:23~80℃ MD:23~80℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电常数 Dielectric constant |
|||
1.10 GHz 1.10 GHz |
ASTM ES7-83 | ||
耗散因数 Dissipation factor |
|||
1.1 GHz 1.1 GHz |
ASTM ES7-83 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.40 mm 0.40 mm |
UL 94 | ||
1.00 mm 1.00 mm |
UL 94 | ||
1.20 mm 1.20 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.2 mm 1.2 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
1.2 mm 1.2 mm |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 类型 1, 2.0 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*3 sp=62mm |
8 80*10*3 |
9 120*10*4 mm |
10 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部 |
朗盛莱茵化学事业部结合橡胶和颜料特种化学品 聚焦点特种化工品业务
多业务线迈入新高管 朗盛于2020年4月进行英国科聚亚企业的回收后,这个特种化工品企业调节了公司组织架构。两根业务线硫化橡胶助剂业务(RAB)和颜料助剂业务(CAB)如今均归于莱因有机化学事业部。 朗盛此次产业结构调整的目地是为了更好地配套设施比原来更关心客户满意度的业务方法。该事业部将在未来承担特种业务下的特异性成份化学物质、特种化工品及其硫化橡胶、塑胶和颜料业应用的生产加工助剂。 “这两根业务线将与别的特种业务有一样的规定和构造,也就代表着能够 解决少量订单信息,”莱因有机化学2017年4月新就任责任人Philipp Junge那样说。Junge先前自2014年底曾承担硫化橡胶助剂业务,改制后的义务范畴仍包含此业务。 颜料助剂业务的新责任人是Dominik Risse,他以前承担朗盛集团公司的合拼与回收作用,如今再次进到经营行业以承担该业务。他先前还曾在朗盛颜料业务就职市场部经理。 莱因有机化学的企业名字过去的125半年度在化工里是取得成功的标示,如今也将是硫化橡胶和颜料业务的公司logo。而润滑液和无卤阻燃剂业务将转到朗盛的助剂事业部。这两个事业部是朗盛此次机构产业结构调整的范畴。 莱因有机化学事业部当今有月1000名职工,为全世界120个我国的超出3000名顾客生产制造2000不同产品。该事业部下有两根业务线: 硫化橡胶助剂业务 RAB业务线为硫化橡胶业供货范畴普遍的预分散化化工品、生产加工助剂、硫化促进剂和填充料表面活性剂、抗日光蜡、脱膜剂、油性记号笔黑墨水及其性能卓越硫化橡胶胶襄。这一事业部在以一个企业名字供货各种各样的商品选择项,为硫化橡胶制造业的全部运用出示商品,另外以自主创新适用这一工业生产的发展趋势。 颜料助剂业务 CAB业务线是领域领跑的性能卓越颜料供应商,为成千上万高规定运用应用最优秀的生产制造设备生产制造有机化学颜料,加工厂坐落于莱沃库森。业务线根据全世界物流仓储互联网为遍及全球的顾客出示服务项目。优异的产品品质、长期性技术专业服务支持、高自主创新能力及考虑范畴普遍的管理制度的合规是这一业务线尤为重要的规定规范。 来源于:PUWORLD |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。