牌号简介 About |
---|
坚硬、结实和坚韧的薄膜是使用最通用的聚乙烯等级LF08262制成的。与优质辛烯基(C8)LLDPE相比,Evalene LF08262具有优异的机械性能,特别适用于要求极高的重型应用场合。EVALENE LF08262可以取代丁烯(C4)LLDPE,降低测量可能性,并提供最大的性能优势作为共挤核心层材料。具有突出的整体强度、优越的刚度、优异的机械性能,符合FDA菲律宾食品接触要求、清真认证的典型应用、重型包装袋、农用薄膜、高性能柔性和工业包装,要求具有优异的抗穿刺和抗撕裂性。 Stiff, strong and tough films are made using EVALENE ® LF08262, the most versatile EVALENE ® grade. EVALENE ® LF08262 has outstanding mechanical properties comparable with premium octene-based (C8) LLDPE, which makes it particularly suitable for very demanding heavy duty applications. EVALENE ® LF08262 can replace butene (C4) LLDPE with downgauging possibilities, and delivers maximum performance benefits as a core layer material in coextrusion. FEATURES Outstanding overall strength Superior stiffness Excellent mechanical properties Meets FDA Philippines food-contact requirements Halal certified TYPICAL APPLICATIONS Heavy duty sacks Agricultural films High-performance flexible and industrial packaging requiring superior puncture and tear resistance |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
0.926 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.80 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
割线模量 Secant modulus 3 |
ASTM D882 | ||
1% 正割,MD:25 µm,吹塑薄膜 1% secant, MD: 25 µ m, blow molded film |
327 | MPa | ASTM D882 |
1% 正割,TD:25 µm,吹塑薄膜 1% secant, TD: 25 µ m, blow molded film |
262 | MPa | ASTM D882 |
拉伸强度 tensile strength 4 |
ASTM D882 | ||
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain 4 |
ASTM D882 | ||
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
% | ASTM D882 | |
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:25 µm,吹塑薄膜 MD: 25 µ m, blow molded film |
g | ASTM D1922 | |
TD:25 µm,吹塑薄膜 TD: 25 µ m, blow molded film |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25 µm,吹塑薄膜 45 °, 25 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Blow(up Ratio) Blow(up Ratio) |
备注 |
---|
2 23°C |
3 25 mm/min |
4 500 mm/min |
【新闻资讯】查看全部
巴斯夫投资Pyrum,聚焦用废轮胎热解油生产高性能化学品
2020-09-23 搜料网资讯: 巴斯夫股份公司计划向Pyrum Innovations AG投资1600万欧元,该公司是一家专门从事废轮胎热解技术的公司,总部位于德国萨尔河畔迪林根(Dillingen/Saar)。 通过这项投资,巴斯 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |