牌号简介 About |
---|
Arlon® 2400是一种聚醚醚酮(PEEK)产品,含有的填充物为玻璃纤维增强材料。 它,在北美洲或欧洲有供货。 主要特性为:耐热。 Arlon® 2400 is a Polyetheretherketone (PEEK) product filled with glass fiber. It is available in Europe or North America. Primary characteristic: heat resistant. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.53 | g/cm³ | ASTM D792 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
90 | ASTM D2240 | |
拉伸模量 Tensile modulus |
11600 | MPa | ASTM D638 |
拉伸强度 tensile strength |
ASTM D638 | ||
屈服 yield |
198 | MPa | ASTM D638 |
断裂 fracture |
198 | MPa | ASTM D638 |
断裂,38℃ Fracture, 38 ℃ |
MPa | ASTM D638 | |
断裂,93℃ Fracture, 93 ℃ |
MPa | ASTM D638 | |
断裂,149℃ Fracture, 149 ℃ |
MPa | ASTM D638 | |
断裂,204℃ Fracture, 204 ℃ |
MPa | ASTM D638 | |
断裂,260℃ Fracture, 260 ℃ |
MPa | ASTM D638 | |
断裂,316℃ Fracture, 316 ℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
-- -- |
MPa | ASTM D790 | |
38℃ 38℃ |
MPa | ASTM D790 | |
93℃ 93℃ |
MPa | ASTM D790 | |
149℃ 149℃ |
MPa | ASTM D790 | |
204℃ 204℃ |
MPa | ASTM D790 | |
260℃ 260℃ |
MPa | ASTM D790 | |
316℃ 316℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ASTM D790 | ||
断裂 fracture |
MPa | ASTM D790 | |
断裂,38℃ Fracture, 38 ℃ |
MPa | ASTM D790 | |
断裂,93℃ Fracture, 93 ℃ |
MPa | ASTM D790 | |
断裂,149℃ Fracture, 149 ℃ |
MPa | ASTM D790 | |
断裂,204℃ Fracture, 204 ℃ |
MPa | ASTM D790 | |
断裂,260℃ Fracture, 260 ℃ |
MPa | ASTM D790 | |
断裂,316℃ Fracture, 316 ℃ |
MPa | ASTM D790 | |
压缩强度 compressive strength 2 |
ASTM D695 | ||
-- -- |
MPa | ASTM D695 | |
38℃ 38℃ |
MPa | ASTM D695 | |
93℃ 93℃ |
MPa | ASTM D695 | |
149℃ 149℃ |
MPa | ASTM D695 | |
204℃ 204℃ |
MPa | ASTM D695 | |
260℃ 260℃ |
MPa | ASTM D695 | |
316℃ 316℃ |
MPa | ASTM D695 | |
剪切强度 shear strength |
ASTM D732 | ||
-- -- 3 |
MPa | ASTM D732 | |
-- -- 4 |
MPa | ASTM D732 | |
38℃ 38℃ 3 |
MPa | ASTM D732 | |
38℃ 38℃ 4 |
MPa | ASTM D732 | |
93℃ 93℃ 3 |
MPa | ASTM D732 | |
93℃ 93℃ 4 |
MPa | ASTM D732 | |
149℃ 149℃ 3 |
MPa | ASTM D732 | |
149℃ 149℃ 4 |
MPa | ASTM D732 | |
204℃ 204℃ 3 |
MPa | ASTM D732 | |
204℃ 204℃ 4 |
MPa | ASTM D732 | |
260℃ 260℃ 3 |
MPa | ASTM D732 | |
260℃ 260℃ 4 |
MPa | ASTM D732 | |
316℃ 316℃ 3 |
MPa | ASTM D732 | |
316℃ 316℃ 4 |
MPa | ASTM D732 | |
断裂弯曲应变 Fracture bending strain |
ASTM D790 | ||
-- -- |
% | ASTM D790 | |
38℃ 38℃ |
% | ASTM D790 | |
93℃ 93℃ |
% | ASTM D790 | |
149℃ 149℃ |
% | ASTM D790 | |
204℃ 204℃ |
% | ASTM D790 | |
260℃ 260℃ |
% | ASTM D790 | |
316℃ 316℃ |
% | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Max Load |
3 Transverse |
4 Axial |
【新闻资讯】查看全部
三菱化学碳纤维加强塑料用于消费奥迪RS 5车顶
2017-08-25 三菱化学株式会社(总部:东京都千代田区;总经理:Hitoshi Ochi,以下简称“MCC”)宣布,其碳纤维复合材料已被用于生产2017年6月推出的奥迪A5系列RS 5高级运动轿跑车的高循环压模(预浸料模压成型 [PCM])车顶。车顶使用PCM工艺制造,并由德国MCC集团公司Wethje Carbon Composites GmbH(以下简称“Wethje”)交付给奥迪。Wethje主要负责用碳纤维增强塑料(CFRP)生产汽车零部件。 随着燃油效率法规和二氧化碳排放控制逐渐 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |