牌号简介 About |
---|
Crystal Clear® 200、202、204和206为水白色透明,专门用于需要澄清的应用。这些硬质聚氨酯浇注树脂只在工作时间和拆卸时间上有所不同。粘度低,易于搅拌和浇注。结晶透明树脂在室温*下固化,收缩率可忽略不计。固化铸件抗紫外线,不易碎。通过添加颜料分散体来获得鲜艳的色彩和色彩效果。应用范围包括封装、制作原型模型、透镜、雕塑复制品、装饰铸件、珠宝、原型模型、特殊效果和道具。Crystal Clear 220和221是较硬的热固化产品,与这些室温相比具有优势。治愈产品。CC220和CC221可在www.smooth-on.com上获得单独的技术公告。 Crystal Clear® 200, 202, 204 and 206 are water white clear and made specifically for applications that require clarity. These rigid urethane casting resins differ only in working and demold times. Low viscosity ensures easy mixing and pouring. Crystal Clear® resins cure at room temperature* with negligible shrinkage. Cured castings are UV Resistant and are not brittle. Vibrant colors and color effects are achieved by adding pigment dispersions. Applications include encapsulation, making prototype models, lenses, sculpture reproductions, decorative cast pieces, jewelry, prototype models, special effects and props. Crystal Clear® 220 and 221 are harder, heat cured products that offer advantages over these room temp. cure products. A separate tech bulletin is available for Crystal Clear® 220 and 221 at www.smooth-on.com. CAUTION: NOT FOR HOME USE. THIS PRODUCT IS FOR INDUSTRIAL USE ONLY. Proper ventilation, A NIOSH Approved Respirator and Protective Clothing (gloves and long sleeves) are required to minimize the risk of inhalation and dermal sensitization. If breathing is affected or a dermal rash develops, immediately cease using this product and seek medical attention. Read SDS before using. |
产品描述 Product Description
厂家:美国Smooth-On
类别:PUR
用途:装饰部件;镜头;成型材料;珠宝;
颜色:清晰/透明
加工条件:浇铸,包封 casting
性能特点: 机械强度好; 着色性好; 透光性好; 低粘度; 收缩性低; 耐候抗UV; Good Rigidity,Good coloring,Good Clarity,Low Viscosity,Low contractility,Weather resistance is good
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.03 | g/cm³ | ASTM D1475 |
特定体积 Specific volume Specific volume |
0.965 | cm³/g | ASTM D1475 |
成型收缩率 Molding Shrinkage Molding shrinkage |
|||
MD MD |
0.10 | % | ASTM D2566 |
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脱模时间 stripping time Stripping time |
|||
23℃ 23℃ |
960 | min | |
补充信息 Supplementary Information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
混合比 Mixing ratio Mixing ratio |
100A:90B by weight | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸模量 Tensile Modulus Tensile Modulus |
MPa | ASTM D638 | |
拉伸强度 Tensile Strength Tensile Strength |
MPa | ASTM D638 | |
断裂伸长率 Elongation at Break Elongation at Break |
% | ASTM D638 | |
弯曲模量 Flexural Modulus Flexural Modulus |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength Flexural Strength |
MPa | ASTM D790 | |
压缩模量 Compressive Modulus Compressive Modulus |
MPa | ASTM D695 | |
压缩强度 Compressive Strength Compressive Strength |
MPa | ASTM D695 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
储存稳定性 STORAGE STABILITY STORAGE Stability |
min | ||
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive Index Refractive Index |
|||
20℃ 20℃ |
% | ||
25℃ 25℃ |
% | ||
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric Strength Dielectric Strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric Constant Dielectric Constant |
|||
100Hz 100Hz |
ASTM D150 | ||
1KHz 1KHz |
ASTM D150 | ||
耗散因数 Dissipation Factor Dissipation Factor |
|||
100Hz 100Hz |
ASTM D150 | ||
1KHz 1KHz |
ASTM D150 | ||
体积电阻率 Volume Resistivity Volume Resistance |
ohm·cm | ASTM D257 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Cure Time |
【新闻资讯】查看全部
一大波装置将投产!年内PE新增560万吨、PP新增669万吨
2021-03-08 搜料网资讯: 一大波装置将投产!年内PE新增560万吨、PP新增669万吨 2020年我国聚烯烃行业正式进入优胜劣汰的大整合阶段。 2021年市场将重新迎来一波投产高峰,聚烯烃仍是产能持续扩 |
一大波装置将投产!年内PE新增560万吨、PP新增669万吨 搜料网资讯:一大波装置将投产!年内PE新增560万吨、PP新增669万吨 2020年我国聚烯烃行业正式进入优胜劣汰的大整合阶段。 2021年市场将重新迎来一波投产高峰,聚烯烃仍是产能持续扩增的一年,且低成本优势将更加明显,原料来源更趋向于多样化。
2020年国内PE原计划新增装置产能为565万吨,增幅将高达27.75%,远高2019年的8.99%。 但受新冠肺炎疫情影响,有部分装置将延后至2021年投产。 数据显示:2020年投产的新装置共有7套,涉及产能为390万吨,此外,还有145万吨的产能延迟至2021年投产。 2021年,目前计划投产的PP装置有11套,涉及产能约为560万吨,较2020年增长22.8%。 其中,一季度增加125万吨,二季度60万吨,三季度170万吨,四季度约60万吨,不确定时间,但有投产计划的装置有两套,涉及产能145万吨。 若均按计划投产,则一、三季度新增的产能较多。
2020年年初PP预计新增10套装置共计475万吨产能,实际8套装置顺利落地,新增产能375万吨。尽管受疫情影响,但2020年新装置投产普遍较为顺利,多数一次试车成功,产能投放率(实际新增产能/预期新增产能)达到了80%,为历史最高。 2021年PP扩能初步统计在554万吨,算上2020年未及投产的龙油石化(二线35万吨)、福基二期(80万吨),2021年PP名义新增产能共计669万吨,新增产能增速为20.1%。新装置投产集中在一、四季度。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。