牌号简介 About |
---|
Amodel® A-4160 L是一种60%玻璃纤维增强的聚邻苯二甲酰胺(PPA),具有高模量、高热偏转温度和优异的抗蠕变性能。这种材料被设计用来代替金属,特别适用于腐蚀敏感的应用。其快速结晶和良好的流动特性允许更短的周期以提高成型生产率。黑色:A-4160 L BK324 Amodel® A-4160 L is a 60% glass reinforced polyphthalamide (PPA) which exhibits high modulus, a high heat deflection temperature, and exceptional creep resistance. This material was designed to replace metal and is particularly suited for corrosion sensitive applications. Its rapid crystallization and good flow characteristics allow shorter cycles for enhanced molding productivity. Black: A-4160 L BK324 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.75 | g/cm³ | ISO 1183/A |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
0.80 | % | ISO 294-4 |
MD MD |
0.50 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.19 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
23300 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
科思创将展示从伤口护理到可穿戴智能贴片的材料解决方案
2022-05-19 在今年2022年5月23日至25日于法国巴黎举行的EWMA会议上,科思创将展示与可穿戴智能贴片和伤口护理有关的创新材料开发。 更加舒适和可持续的可穿戴设备 可穿戴式贴片传感器(智能贴 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |