牌号简介 About |
---|
SARLINK ME-2390B-01 BLK是一种通用的热塑性弹性体,用于汽车应用。SARLINK ME-2390B-01 BLK是一种高硬度、低密度等级的产品,具有良好的可塑性。该等级适用于注塑成型。 Sarlink ME-2390B-01 BLK is a general purpose Thermoplastic Elastomer used in automotive applications. Sarlink ME-2390B-01 BLK is a high hardness, low density grade exhibiting good moldability characteristics. This grade is suitable for injection molding. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A,1 秒,注塑成型 Shore A, 1 second, injection molding |
90 | ISO 868 | |
邵氏 A,5 秒,注塑成型 Shore A, 5 seconds, injection molding |
89 | ISO 868 | |
邵氏 A,15 秒,注塑成型 Shore A, 15 seconds, injection molding |
88 | ISO 868 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
ISO 37 | ||
TD,100% 应变 TD, 100% strain |
4.20 | MPa | ISO 37 |
MD,100% 应变 MD, 100% strain |
5.49 | MPa | ISO 37 |
拉伸应变 Tensile strain 2 |
ISO 37 | ||
TD,断裂 TD, fracture |
% | ISO 37 | |
流量,断裂 Flow rate, fracture |
% | ISO 37 | |
撕裂强度 tear strength 3 |
ISO 34-1 | ||
TD TD |
kN/m | ISO 34-1 | |
MD MD |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation 4 |
ISO 815 | ||
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
90℃,70 hr 90℃,70 hr |
% | ISO 815 | |
125℃,70 hr 125℃,70 hr |
% | ISO 815 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air 5 |
ISO 188 | ||
TD:110℃,1008 hr TD:110℃,1008 hr |
% | ISO 188 | |
MD:110℃,1008 hr MD:110℃,1008 hr |
% | ISO 188 | |
TD:100% 应变 110℃,1008 hr TD: 100% strain at 110 ℃, 1008 hr |
% | ISO 188 | |
MD:100% 应变 110℃,1008 hr MD: 100% strain at 110 ℃, 1008 hr |
% | ISO 188 | |
TD:125℃,168 hr TD:125℃,168 hr |
% | ISO 188 | |
MD:125℃,168 hr MD:125℃,168 hr |
% | ISO 188 | |
MD:100% 应变 125℃,168 hr MD: 100% strain 125 ℃, 168 hr |
% | ISO 188 | |
TD:100% 应变 168℃,125 hr TD: 100% strain 168 ℃, 125 hr |
% | ISO 188 | |
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
ISO 188 | ||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 6 |
ISO 188 | ||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 7 |
ISO 188 | ||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 8 |
ISO 188 | ||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 6 |
ISO 188 | ||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 7 |
ISO 188 | ||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 8 |
ISO 188 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
g/10min | ASTM D1238 | |
熔体表观粘度 Apparent viscosity of melt |
|||
200℃,206 sec^-1 200℃,206 sec^-1 |
Pa·s | ASTM D3835 | |
特殊值 Special value |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
TD,断裂 TD, fracture |
MPa | ISO 37 | |
MD,断裂 MD, fracture |
MPa | ISO 37 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 20 in/min |
3 B 方法,直角形试样(不割口), 20 in/min |
4 类型 A |
5 类型 1 |
6 Instant |
7 5 sec |
8 15 sec |
【新闻资讯】查看全部
ADNOC拟建天然气制甲醇工厂
2022-03-20 近日,阿布扎比国家石油公司(ADNOC)和总部位于瑞士的船舶管理公司Proman宣布,计划在阿联酋鲁韦斯的阿布扎比化学品衍生物公司(塔齐兹)化工园区建设一座180万吨/年的天然气制甲醇厂。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |