牌号简介 About |
---|
IE-3081是一种硬质聚氨酯,适用于室温手工或真空辅助铸造法。在不使用汞、MOCA或TDI的情况下,室温固化可获得优异的物理性能。IE-3081的混合粘度非常低。它是理想的配色,因为它的中性半透明外观。 IE-3081 is a rigid polyurethane formulated for room temperature hand-batch or vacuum assisted casting methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA or TDI. IE-3081 has a very low mixed viscosity. It is ideal for color-matching due to its neutral semi-transparent appearance. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
Hardener Hardener |
1.03 | g/cm³ | |
固化处理 Curing treatment |
1.08 | g/cm³ | |
基体树脂 Matrix resin |
1.10 | g/cm³ | |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 到 1.0 | % | ASTM D2566 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲模量 Bending modulus |
1380 | MPa | ASTM D790 |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
粘度 viscosity |
|||
25℃ 25℃ 2 |
Pa·s | ||
25℃ 25℃ 3 |
Pa·s | ||
25℃ 25℃ 4 |
Pa·s | ||
固化时间 Curing time |
|||
25℃ 25℃ |
hr | ||
胶凝时间 Gelation time |
min | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
脱模时间 stripping time |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Resin |
3 Mixed |
4 Hardener |
【新闻资讯】查看全部 ![]()
国立科技进入生物降解材料赛道
2021-09-15 搜料网资讯: 近日,广东国立科技股份有限公司发布向特定对象发行股票预案,拟向不超过35名(含)特定投资者,募资不超过2.82亿元,用于生物降解材料及制品产业化建设项目、生物降 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |