牌号简介 About |
---|
HTA 001HD5是一种高分子量高密度聚乙烯薄膜级。HTA 001HD5薄膜具有优异的冲击韧性和高硬度。 HTA 001HD5 is a high molecular weight HDPE film grade. Films made from HTA 001HD5 exhibit excellent impact and toughness properties as well as high stiffness. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,21.6kg 190℃,21.6kg |
9.0 | g/10min | ASTM D1238 |
190℃,5.0kg 190℃,5.0kg |
0.32 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD 1% secant, MD |
1200 | MPa | ASTM D882 |
1% 正割,TD 1% secant, TD |
1200 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
41.0 | MPa | ASTM D882 |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
MD,断裂 MD, fracture |
MPa | ASTM D882 | |
TD,断裂 TD, fracture |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD MD |
g | ASTM D1922 | |
TD TD |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
全球结束使用含铅汽油
2021-09-02 搜料网资讯: 内罗毕消息:联合国环境规划署8月30日宣布,随着阿尔及利亚的加油站今年7月停止供应含铅汽油,全球已结束使用这种危害健康又污染环境的汽油品种。 联合国环境规划 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |