牌号简介 About |
---|
POM共聚物易流动注射成型,如C 13021,但在整个软管允许温度范围内具有较高的强度、刚度和硬度;对溶剂、燃料和强碱具有良好的耐化学性以及良好的水解性;对热降解和氧化降解具有较高的耐化学性。如果厚度超过1 mm,紫外线添加剂的燃烧速率为ISO 3795和FMVSS 302<75 mm/min。适用范围:对于对强度、刚度和硬度要求较高的模件,fmvss=联邦机动车辆安全标准(美国) POM copolymer Easy flowing Injection molding type like C 13021, but with higher strength, rigidity and hardness over the entire permissible temperature range for HOSTAFORM; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation. With UV Additives Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more than 1 mm. Ranges of applications: For molded parts with higher requirements to strength, rigidity und hardness, FMVSS = Federal Motor Vehicle Safety Standard (USA) |
产品描述 Product Description
厂家:美国塞拉尼斯 Celanese
类别:POM共聚 Copolymer Polyformaldehyde
性能特点: 耐化学性; 耐水解; 易流动; 耐燃油; 耐候抗UV; 耐碱; Weather resistance is good,Alkali resistant,Hydrolysis stability,Good liquidity,Solvent resistance,Fuel resistance
紫外线:UV Stabilized
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.41 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
190℃,2.16 kg 190℃,2.16 kg |
12.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
1.8 | % | ISO 294-4 |
MD MD |
2.0 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
0.65 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/1A/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2/1A/50 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
% | ISO 527-2/1A/50 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10°C/min |
【新闻资讯】查看全部
专为电动汽车量身定制,无铜和无卤素热稳定剂用于PA
2023-01-12 扫描上图二维码,可以免费下载 搜料 APP 确保聚酰胺等工程塑料热稳定性的添加剂是汽车零部件的关键成分。然而,随着电动汽车数量的激增,金属部件(如包覆成型的传感器)的潜在腐 |
专为电动汽车量身定制,无铜和无卤素热稳定剂用于PA
确保聚酰胺等工程塑料热稳定性的添加剂是汽车零部件的关键成分。然而,随着电动汽车数量的激增,金属部件(如包覆成型的传感器)的潜在腐蚀已成为一个问题。为了解决这个问题,Brüggemann开发了一种不含铜和卤素的中性长期热稳定剂。
Bruggolen TP-H2217是专门为增强和非增强脂肪族聚酰胺(PA)开发的,具有无金属和无卤阻燃特性。它满足电气和电子应用的需求,包括电力运输。Brüggemann表示,尽管这种添加剂效率很高,但它对金属零件没有腐蚀作用,也不会以任何方式显著改变其保护的聚合物的电性能。
Bruggolen TP-H2217在使用30%玻璃纤维增强PA66时已证明其长期稳定的效率。在170°C下暴露8000小时后,拉伸强度值仍大于初始值的50%。
在电动汽车应用中使用任何添加剂的关键要求是这些应用的阻燃性不会受到损害。Bruggolen TP-H2217在这方面是中性的,Bruggolen TP-H2217也是中性的,它是Brüggemann的一种新型流动增强剂,用于将玻璃纤维增强的PA加工成具有长流动路径的薄壁/复杂零件。
Brüggemann产品经理Kristina Frädrich博士评论道:“通过使用Bruggolen TP-H2217,配混厂商首次可以生产出既满足UL94 V-0级别,又具有电中性且可以满足高温下永久耐热性的聚酰胺材料,该材料可以满足电动汽车不断提升的要求。有了这种苯酚或胺基牌号都无法提供的组合性能,Brüggemann大大提高了热稳定剂的标准。”
Bruggolen TP-H2217是一种易于加工的粒状母料,3%的添加量足以满足实验室测试中的许多应用。
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- 奥迪刹车灯框
- 2019-07-31 0
- Hostaform POM共聚物非常坚硬和僵硬,是奥迪A4中的第三个制动灯就是目前使用的Xap级hostaform车辆。由于其暴露在后窗后面,因此软管式XAP部件必须具有良好的紫外线稳定性。另外一个问题是温度的
- 阅读全文
奥迪刹车灯框
奥迪A4中的第三个制动灯就是目前使用的Xap级hostaform车辆。由于其暴露在后窗后面,因此软管式XAP部件必须具有良好的紫外线稳定性。另外一个问题是温度的极端差异,这反过来需要良好的热变形阻力和抗冻性。制动灯的颜色必须与车辆的颜色匹配。
收起
抱歉!暂无数据。