牌号简介 About |
---|
冷热水管道用高密度湿固化聚乙烯化合物。适用于在140°F和80 psi工作条件下连续工作的SDR 9管道应用。Pexidan® L/T(包括L/T Eclipse)是一种高密度PEX系统,由硅烷接枝碱化合物A-1001和催化剂母料CAT-003组成。当以适当比例混合和挤压时,双组分系统会产生一种材料,该材料可通过暴露于水分或90-95°C的热水中进行交联。Pexidan® L/T由NSF国际根据标准14和61以及加拿大标准协会标准B137.5列出。根据ASTM F 876和ASTM F 2023进行的NSF认证证明其具有优异的耐高温氯化水氧化性能。Pexidan® L/T可用于国内连续循环系统,并被NSF列为NSF PW CL5/PEX 5006材料。 High density moisture curable polyethylene compound for hot and cold water plumbing pipe. Suitable for SDR 9 pipe applications in continuous service at operating conditions of 140°F and 80 psi. Pexidan® L/T (including L/T Eclipse) is a high density PEX System consisting of a silane grafted base-compound A-1001 and a catalyst masterbatch CAT-003. When mixed and extruded in the proper proportions, the two-component system results in a material that is crosslinkable by exposure to moisture or by immersion in hot water at 90-95°C. Pexidan® L/T is listed by NSF International to Standards 14 and 61 and to Canadian Standards Association standard B137.5. NSF certification to ASTM F 876 and ASTM F 2023 testifies to its superior resistance to oxidation by hot, chlorinated water. Pexidan® L/T is permitted to be used in domestic continuous re-circulation systems and is listed by NSF as a NSF-pw CL5 / PEX 5006 material. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.944 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
交叉结合的程度 The degree of cross combination |
> 70 | % | ASTM D2765 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
124 | ℃ | ASTM D1525 |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-100~85℃ MD:-100~85℃ |
1.5E-4 | 1/℃ | ASTM D696 |
比热 specific heat |
|||
23℃ 23℃ |
J/kg/℃ | ||
氧感应时间 Oxygen sensing time |
min | ASTM D3895 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
高温伸长率 High temperature elongation 2 |
内部方法 | ||
负荷下伸长率:150℃ Elongation under load: 150 ℃ |
% | 内部方法 | |
permanent elongation(set) after cooling:150℃ permanent elongation(set) after cooling:150℃ |
% | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
ISO 527-2 | ||
-40℃ -40℃ |
MPa | ISO 527-2 | |
0℃ 0℃ |
MPa | ISO 527-2 | |
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ASTM D638 | ||
屈服 yield |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ISO 178 | ||
-40℃ -40℃ |
MPa | ISO 178 | |
0℃ 0℃ |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ISO 178 | |
流体静力学设计基础 - @ 68% DOC Fundamentals of Hydrostatic Design - @ 68% DOC |
ASTM D2837 | ||
82℃ 82℃ |
MPa | ASTM D2837 | |
93℃ 93℃ |
MPa | ASTM D2837 | |
23℃ 23℃ |
MPa | ASTM D2837 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 15 minutes, 0.2 N/mm² load |
【新闻资讯】查看全部
巴西去年燃料销量创新高
2022-02-27 近日,巴西国家石油管理局(ANP)公布的统计数据显示,2021年,得益于新冠肺炎疫苗接种加快和巴西国内经济回升,巴西汽油、柴油、乙醇和煤油等燃料总计销量达1395亿升,比上一年增长 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |