牌号简介 About |
---|
石油管道专用材料超高韧性,强度好,耐低温性能优异,吸水率低,加工收缩率小,成型加工性能好。主要用于汽车制动管、输油管、穿线管、空调用软管管等,在要求耐低温、高韧性的情况下,完全可以替代PA11、PA12。 Special Purpose Material for Oil Pipeline Superhigh toughness, better intensity, outstanding low temperature resistance, lower water absorption, smaller inprocess shrinkage rate, good molding processibility. It is mainly used in the auto's brake-pipe, oil pipeline, threading pipe, hose pipe for air conditioning use, etc. tubes and pipes, as well as other circumstances when demanding for low temperature resistance and high toughness, can totally substitute for PA11 and PA12. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
> 50.0 | MPa | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
> 300 | % | |
弯曲模量 Bending modulus |
> 200 | MPa | |
弯曲强度 bending strength |
< 13.0 | MPa | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
无断裂 | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
兰州石化进步国产化助剂使用比例增效明显
2016-02-26 日前,记者获悉,今年兰州石化公司乙烯厂提高国产化助剂使用比例等攻关项目增效显著,1至11月,这个厂共增效179万元。 该厂在进行助剂评价的基础上,重新制定生产方案,精细调整相关工艺参数,提高三乙基铝等国产助剂使用比例,增效近500万元。 乙烯装置“降低稀释蒸汽压力,减少中压蒸汽用量,降低乙烯能耗”这一项目增效也较为突出。乙烯车间通过摸索裂解炉生产规律,查找大量原始数据,翻阅最初设计附件,同时开展工业试验,发现由于单通道进料量太低导致物料和稀释蒸汽在通道中发生 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |