牌号简介 About |
---|
维斯特利特G 217是一种低至中分子量均聚物混合树脂,用于塑料溶胶配方中的配方工具,它改善了空气释放性能,降低了废品率。它降低了高剪切粘度,提高了“易于涂层”的性能,从而使塑性溶胶涂层更加均匀,提高了生产线的生产时间。它降低了粘度老化特性,增加了塑料溶胶的使用(使用寿命)。它降低了薄膜或涂层产品的表面光泽度,从而减少了表面阻塞,提高了处理能力。VestoLIT G 217推荐用于固体和泡沫塑料溶胶应用,如涂层织物、流延膜和涂层、泡沫垫和垫。 VESTOLIT G 217 is a low to medium molecular weight homopolymer blending resin intended for use as a formulation tool in plastisol formulations.It improves air release performance resulting in reduced scrap rates. It decreases high shear viscosity providing an improved 'ease of coating' performance resulting in a more uniform plastisol coating and improving line up time. It reduces viscosity aging characteristics, providing increased plastisol usage (pot life). It reduces surface gloss of films or coated products resulting in less surface blocking and improved handling. VESTOLIT G 217 is recommended for solid and foamed plastisol applications such as coated fabric, cast films and coatings, foam mats and pads. |
技术参数 Technical Data | |||
---|---|---|---|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze 5 |
|||
Fused 5 mins,177℃ Fused 5 mins,177℃ 5 |
54 | % | 内部方法 |
光泽度 gloss 6 |
|||
60 Degree Fused 5 mins @ 350F 60 Degree Fused 5 mins @ 350F 6 |
18 | % | 内部方法 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Residual Vinyl Chloride Monomer Residual Vinyl Chloride Monomer 9 |
< 5 | ppm | 内部方法 |
挥发性 volatility 10 |
0.050 | % | 内部方法 |
聚合过程 polymerization process |
悬挂 | ||
凝胶温度 Gel temperature 11 |
|||
PP PP 11 |
℃ | 内部方法 | |
乙烯基扩散计 Vinyl diffusion meter 12 |
µm | 内部方法 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
K-Value K-Value 1 |
内部方法 | ||
表观松态密度 Apparent density of loose states 2 |
g/cm³ | 内部方法 | |
固有粘度 Intrinsic viscosity |
ASTM D1243-60-A | ||
颗粒大小 Particle size 3 |
内部方法 | ||
< 52 Micron < 52 Micron |
% | 内部方法 | |
< 74 Micron < 74 Micron |
% | 内部方法 | |
平均粒径 Average particle size |
µm | 内部方法 | |
相对粘度 Relative viscosity 4 |
内部方法 | ||
布络克菲尔德粘度 Brookfield viscosity 7 |
内部方法 | ||
初始粘度@ 2 rpm Initial viscosity @ 2 rpm |
Pa·s | 内部方法 | |
初始粘度@ 2 rpm Initial viscosity @ 2 rpm |
Pa·s | 内部方法 | |
一天粘度@ 2 rpm One day viscosity @ 2 rpm |
Pa·s | 内部方法 | |
一天粘度@ 20 rpm One day viscosity @ 20 rpm |
Pa·s | 内部方法 | |
切断流出 Cut off the outflow 8 |
|||
95 psi 95 psi 8 |
g/10 min | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Correlation, 0.5g/100ml |
3 VESTOLIT STP 1169 |
4 VESTOLIT DFT 1466 |
5 Correlation, Cyclohexanone 1% |
6 VESTOLIT ALTC 66 (with provided formulation) |
7 VESTOLIT ALTC 65 (with provided formulation) |
8 VESTOLIT ALTC 22 (with provided formulation) |
9 VESTOLIT ALTC 23 (with provided formulation) |
10 VESTOLIT STP 1005 |
11 VESTOLIT STP 1242 |
12 VESTOLIT ALTC 29 (with provided formulation) |
13 VESTOLIT STP 1203 (with provided formulation) |
【新闻资讯】查看全部
广州抽查食品用塑料工具产品
2016-08-05 广州市质量技术监督局官网近日公布2016年广州市食品用塑料工具产品质量监督抽查结果,在广州市生产领域抽查了45家企业生产的53批次产品,经检验,有1批次产品不合格,不合格产品发现率为1.9%。 本次食品用塑料工具的监督抽查,依据GB/T 17876-2010《包装容器 塑料防盗瓶盖》、QB/T 1868-2004《聚对苯二甲酸乙二醇酯(PET)碳酸饮料瓶》、QB 2357-1998 《聚酯(PET)无汽饮料瓶》、QB 2460-1999《聚碳酸酯(PC)饮用水罐》、 QB/ |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |