牌号简介 About |
---|
类型:聚醚基级挤出和注塑级特点:具有优异的水解稳定性、耐真菌性、良好的低温柔韧性,符合FDA(21 CFR 177.1680、177.2600)、RoHS、ISO 10993和USP VI应用:电子零件、电线电缆、医疗产品等。 TYPE: Polyether-based grade Extrusion and injection molding grade FEATURES: Excellent hydrolytic stability, fungus resistance, good low-temperature flexibility, complies with FDA(21 CFR 177.1680, 177.2600), ROHS, ISO 10993 & USP VI Applications: Electronic parts, wire & cable, medical products, etc |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.13 | g/cm³ | ASTM D792 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
断裂 fracture |
38.0 | MPa | ASTM D412 |
100% 应变 100% strain |
12.0 | MPa | ASTM D412 |
300% 应变 300% strain |
25.0 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
380 | % | ASTM D412 |
撕裂强度 tear strength |
kN/m | ASTM D624 | |
压缩形变 Compression deformation |
ASTM D395 | ||
23℃,24 hr 23℃,24 hr |
% | ASTM D395 | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D3418 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ASTM D2240 | ||
DIN Abrasion DIN Abrasion |
mm³ | ISO 4649 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
聚赛龙加强阻燃PET塑料
2018-02-06 PET塑料(聚对苯二甲酸乙二醇酯)是热塑性聚酯中最主要的品种之一,1946年英国公开了第一个制备PET塑料的专利,1953年美国DuPont公司最早实现了PET塑料的工业化生产。初期的PET几乎全部用于合成纤维,到了上世纪80年代,PET塑料作为工程塑料有了突破性的进展,成为继尼龙、聚碳酸酯、聚甲醛、聚苯醚之后的第五大工程塑料。PET塑料是发展极为迅速的塑料品种,2016年全球PET的产量已经超过7670万吨,预计2020年全球PET产量将达11017万吨。 PET作为工程 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |