牌号简介 About |
---|
WRM124是一种低密度聚乙烯,具有良好的光泽度和流动/韧性比,同时具有较低的翘曲倾向。WRM124是专为密封盖、家庭用品和玩具设计的高流量等级。WRM124适用于食品接触应用,符合美国食品药品管理局CFR 21 177.1520第(c)段第2.1项的要求。 Alkathene WRM124 is a high flow low density polyethylene which offers excellent gloss and flow/toughness ratio coupled with a low tendency to warp. Alkathene WRM124 is designed specifically for reseal lids, housewares and toys. WRM124 is not recommended for high stress crack resistance applications. Suitability for use in any application should be determined by appropriate performance testing. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.920 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
22 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
100%乳化剂,F50 100% emulsifier, F50 |
0.317 | hr | ASTM D1693 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-40℃ -40℃ |
无断裂 | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
45.0 | ℃ | ASTM D648 |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength 1 |
|||
屈服 yield 1 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 1 |
|||
断裂 fracture 1 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
【新闻资讯】查看全部
亨斯迈宣布2021年第四季度和全年收益
2022-02-17 2021年第四季度净收入为6.07亿美元,上年同期净收入为3.6亿美元;2021年第四季度每股摊薄收益为2.73美元,上年同期每股摊薄收益为1.54美元。 2021年第四季度调整后净收入为2.07亿美元, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |