牌号简介 About |
---|
Ebarta AH 100是一种非常薄的未填充环氧树脂,可与不同的硬化剂一起使用。根据应用情况,合适的硬化剂可与树脂AH 100混合。这种树脂/硬化剂混合物价格低廉,因此适合用作硅砂辅助底片的粘合剂。应用硅树脂和辅助负离子粘合树脂织物粘合树脂填料性能无填充低成本低粘度 ebalta AH 100 is a very thin, unfilled epoxy resin, which can be used with different hardeners. Depending on the application the suitable hardener can be mixed with the resin AH 100. This resin/hardener-mixture is inexpensive and therefore suitable as binder for silica sand auxiliary negatives. Applications Bonding resin for silica sand auxiliary negatives Laminating resin for fabrics Bonding resin for fillers Properties unfilled low cost low viscosity |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
20 到 40 | kJ/m² | ISO 179 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
树脂 resin |
按重量计算的混合比: 100 | ||
硬化法 Hardening method |
按重量计算的混合比: 20 | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
20℃ 20℃ |
1.10 到 1.14 | g/cm³ | |
粘度 viscosity |
|||
25℃ 25℃ |
0.64 到 0.66 | Pa·s | |
固化时间 Curing time |
|||
20℃ 20℃ |
hr | ||
储存稳定性 storage stability 2 |
|||
20 ℃ 20 ℃ 2 |
min | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 7619 | ||
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ISO 604 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 200 g |