牌号简介 About |
---|
SABIC® LLDPE 6318BE是一种用于浇铸薄膜的己烯线性低密度聚乙烯树脂。该产品经过特殊配方设计,在高温下具有最佳的热稳定性,用于铸膜挤出。该级薄膜具有良好的光学性能、韧性、抗穿刺性和撕裂强度。后缀e表示欧洲血统。应用SABIC® LLDPE 6318BE树脂通常用于托盘拉伸包装(预拉伸)、高性能拉伸膜以及其他需要高强度的单层和共挤膜应用。还建议与乙烯/丁烯共聚物LLDPE和LDPE混合以提高强度。本产品不适用于任何医药/医疗应用,也不得用于任何医药/医疗应用。 SABIC® LLDPE 6318BE is a hexene linear low density polyethylene resin for cast film applications. The product has been specially formulated for optimum thermal stability at high temperatures used in cast film extrusion. Films produced from this grade exhibit good optical properties, toughness, puncture resistance and tear strength. The suffix E denotes European origin. Application SABIC® LLDPE 6318BE resin is typically used for pallet stretch wrap (pre-stretch), high performance draw down films and other mono layer and coextruded film applications where high strength is required.The grade is also suggested for blending with ethylene/butene copolymer LLDPE and LDPE for improving strength. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:LLDPE Linear low density polyethylene
用途:薄膜;流延薄膜;拉伸缠绕;混合;
加工条件:流延薄膜
性能特点: 热稳定性好; 机械强度好-撕裂; 抗氧化; 己烯共聚单体; 低密度; 韧性好; 光学性能; 抗穿孔性; Good flexibility,Optical performance,Inoxidizability,Low density,Good tear strength,Puncture Resistant,Hexene copolymers,Heat Stabilized
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.920 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
3.2 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 | µm | |
Elastic Recovery(铸造薄膜,20.0 µm) Elastic Recovery (cast film, 20.0 µ m) |
56 | % | ASTM D5459 |
Protrusion Puncture Resistance - 铸造薄膜(20.0 µm) Corrosion Function Resistance - Cast thin film (20.0 µ m) |
2.70 | J | ASTM D5748 |
Retention Force(60 sec,20.0 µm) Retention Force(60 sec,20.0 µm) 1 |
g | ||
Stress Retention(铸造薄膜,20.0 µm) Stress Retention (cast film, 20.0 µ m) |
% | ASTM D5459 | |
Ultimate Pre(stretch Level 铸造薄膜,20.0 µm) Ultimate Pre-stretch Level - Cast Film (20.0 µm) |
% | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,20 µm,铸造薄膜 45 °, 20 µ m, cast thin film |
ASTM D2457 | ||
雾度 Haze |
|||
20.0 µm,铸造薄膜 20.0 µ m, cast thin film |
% | ASTM D1003A | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
落锤冲击 Drop hammer impact |
|||
20.0 µm,铸造薄膜 20.0 µ m, cast thin film |
J/cm | ISO 7765-2 | |
Peel Cling Peel Cling 2 |
ASTM D5458 | ||
0% pre-stretch:20.0 µm 0% pre-stretch:20.0 µm |
g/2.5 cm | ||
200% pre-stretch:20.0 µm 200% pre-stretch:20.0 µm |
g/2.5 cm | ||
撕裂强度 tear strength 3 |
|||
TD,20 µm TD,20 µm 3 |
kN/m | ISO 6383-2 | |
memo_intro memo_intro |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Cast Film |
【新闻资讯】查看全部
晓星T&C开发出新型尼龙,可用于氢能汽车
2022-09-13 扫描上图二维码,可以免费下载 搜料 APP 韩国纤维制造商晓星TC最近表示,已成功开发出一种新型尼龙,用于制造氢动力汽车储氢罐的内胆。 内胆是燃料箱中的一个容器,用于储存氢气 |
晓星T&C开发出新型尼龙,可用于氢能汽车 韩国纤维制造商晓星T&C最近表示,已成功开发出一种新型尼龙,用于制造氢动力汽车储氢罐的内胆。内胆是燃料箱中的一个容器,用于储存氢气并防止其泄漏。 晓星T&C开发的尼龙材料比通常用于氢气罐的金属材料轻70%,比高密度聚乙烯(HDPE)轻50%。 同时,该公司表示,它在防止氢泄漏方面比其他类型的金属有效30%,比HDPE有效50%。 由其他类型金属制成的内胆更重,并且随着时间的推移变得不耐用。然而,由新尼龙制成的内胆可以保持其耐用性,因为它们不会吸收或释放过多的氢气。 HDPE内胆用于制造高达400巴的高压容器,这不足以承受氢气汽车通常要求的700巴压力。 该公司表示,尼龙制成的内胆可以承受零下40℃至零上85℃的极端温度。
上搜料工程塑料超市www.soliao.com,可以直达现货商城,全部商品都是原厂原包真货,24小时发货,全国含税含运费。
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。