| LEXAN™ LUX9610树脂是一种7 MFR聚碳酸酯，MVR为7。紫外线稳定。非溴化和非氯化阻燃剂，UL94 V0额定值。UL746C f2额定值。透明等级。具有高光学清晰度和抗冲击性。注塑成型。 LUX9610 is a UV stabilized flame retardant transparent PC featuring non brominated and non chlorinated FR system with good flow and thin wall FR performance providing good color stability under heat exposure. Developed for lightguide and LED applications. It meets WEEE/RoHS requirements for various applications. |
产品描述 Product Description
用途：LEDs;
颜色：清晰/透明,清晰/透明
加工条件：注射成型 Injection Molding
性能特点： 无卤; 防火阻燃等级V-0; 高粘度; 颜色稳定; 阻燃; 耐候抗UV; 易流动; Halogen free,V-0,Flame Characteristics,Weather resistance is good,High Viscosity,Good color stability,Good liquidity
| 技术参数 Technical Data | |||
|---|---|---|---|
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell Hardness Rockwell hardness |
118 | R | ASTM D-785 |
|
拉伸应力 Tensile Stress Tensile Stress |
|||
|
屈服 yield, 50 mm/min Yield, 50 mm/min |
62 | MPa | ISO 527 |
|
断裂 break, 50 mm/min Break, 50 mm/min |
58 | MPa | ISO 527 |
|
拉伸应变 Tensile Strain Tensile Strain |
|||
|
屈服 yield, 50 mm/min Yield, 50 mm/min |
6 | % | ISO 527 |
|
断裂 break, 50 mm/min Break, 50 mm/min |
77 | % | ISO 527 |
|
拉伸模量 Tensile Modulus Tensile Modulus |
|||
|
1 mm/min 1 mm/min |
MPa | ISO 527 | |
|
弯曲应力 Flexural Stress Flexural Stress |
|||
|
屈服 yield, 2 mm/min Yield, 2 mm/min |
MPa | ISO 178 | |
|
弯曲模量 Flexural Modulus Flexural Modulus |
|||
|
2 mm/min 2 mm/min |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength Izod Unnotched Impact strength of cantilever beam |
|||
|
23℃ 23℃ |
J/m | ASTM D4812 | |
|
80*10*3 +23°C 80*10*3 +23°C |
KJ/m² | ISO 180/1U | |
|
80*10*3 -30°C 80*10*3 -30°C |
KJ/m² | ISO 180/1U | |
|
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
|||
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
80*10*3 +23°C 80*10*3 +23°C |
KJ/m² | ISO 180/1A | |
|
80*10*3 -30°C 80*10*3 -30°C |
KJ/m² | ISO 180/1A | |
|
多轴向仪器化冲击能量 Instrumented Impact Total Energy Multiaxial Instrumented Impact Total Energy |
J | ISO 6603 | |
|
简支梁缺口冲击强度 Charpy notch Impact strength Charpy notch Impact strength |
|||
|
23℃，80*10*3 sp=62mm 23℃，80*10*3 sp=62mm |
kJ/m² | ISO 179/1eA | |
|
-30℃，80*10*3 sp=62mm -30℃，80*10*3 sp=62mm |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Izod Unnotched Impact strength Charpy Unnotch Impact strength |
|||
|
23℃，80*10*3 sp=62mm 23℃，80*10*3 sp=62mm |
kJ/m² | ISO 179/1eU | |
|
-30℃，80*10*3 sp=62mm -30℃，80*10*3 sp=62mm |
kJ/m² | ISO 179/1eU | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
线性热膨胀系数 CTE Linear coefficient of thermal expansion CTE |
|||
|
-40℃~40℃，流动 flow -40 ℃~40 ℃, flowing flow |
×10-5/℃ | ASTM E831 | |
|
-40℃~40℃，横向 xflow -40 ℃~40 ℃, horizontal xflow |
×10-5/℃ | ASTM E831 | |
|
比热 Specific Heat Specific Heat |
J/g/℃ | ASTM C351 | |
|
导热系数 Thermal Conductivity |
W/m/℃ | ASTM C177 | |
|
球压测试 Ball Pressure Test Ball Pressure Test |
|||
|
123℃-127℃ 123℃-127℃ |
IEC 60695-10-2 | ||
|
维卡软化温度 Vicat Softening Temp Vicat Softening Temperature |
|||
|
B/50 B/50 |
℃ | ISO 306 | |
|
B/120 B/120 |
℃ | ISO 306 | |
|
热变形温度 HDT Hot deformation temperature HDT |
|||
|
1.8 MPa 1.8 MPa |
℃ | ISO 75/Af | |
|
相对温度指数 Relative Temp Index Relative Temperature Index |
|||
|
电气 Elec Electrical Elec |
℃ | UL-746B | |
|
机械冲击 Mech w/impact Mechanical impact Mech w/impact |
℃ | UL-746B | |
|
非机械冲击 Mech w/o impact Non mechanical impact Mech w/o impact |
℃ | UL-746B | |
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
吸水率 Water Absorption Water Absorption |
|||
|
100℃ 100℃ |
% | ISO 62 | |
|
23℃ 23℃ |
% | ISO 62 | |
|
密度 Density Density |
g/cm³ | ISO 1183 | |
|
成型收缩率 Mold Shrinkage Mold Shrinkage |
|||
|
流动 flow，3.2 mm Flow, 3.2 mm |
% | 内部 | |
|
吸湿性 Moisture Absorption Moisture Absorption |
ISO 62 | ||
|
23℃。50%r.h. 23℃。50%r.h. |
|||
|
熔体体积流动速率 Melt Volume Rate Melt Volume Rate |
|||
|
300℃，1.2 kg 300℃，1.2 kg |
cm³/10min | ISO 1133 | |
|
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
透光率 Light Transmission Light Transmission |
|||
|
2.54 mm 2.54 mm |
% | ASTM D1003 | |
|
雾度 Haze Haze |
|||
|
2 mm 2 mm |
% | 内部 | |
|
折射率 Refractive Index |
ISO 489 | ||
|
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
介电强度 Dielectric Strength Dielectric Strength |
|||
|
空气 air，3.2 mm Air, 3.2 mm |
kV/mm | ASTM D149 | |
|
介电常数 Relative Permittivity Relative permittivity |
|||
|
50/60 Hz 50/60 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation Facto Dissipation Factor |
|||
|
50/60 Hz 50/60 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
热丝引燃 Hot Wire Ignition Hot wire ignition |
PLC Code | UL 746A | |
|
高电压电弧起痕速率 High Ampere Arc Ign, surface High Ampere Arc Ign, surface |
PLC Code | UL 746A | |
|
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
PLC Code | UL 746A | |
|
体积电阻率 Volume Resistivity Volume Resistance |
ohm·cm | IEC 60093 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
UL阻燃等级 UL Recognized UL flame retardant rating UL Recognized |
|||
|
0.3 mm 0.3 mm |
UL 94 | ||
|
1.5 mm 1.5 mm |
UL 94 | ||
|
灼热丝可燃性指数 Glow Wire Flammability Index Glow Wire Flammability Index |
|||
|
0.8 mm 0.8 mm |
℃ | IEC 60695-2-12 | |
|
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
|
1 mm 1 mm |
℃ | IEC 60695-2-12 | |
|
灼热丝起燃温度 Glow Wire Ignitability Temperature Glow Wire Ignitability Temperature |
|||
|
1.0 mm 1.0 mm |
℃ | IEC 60695-2-13 | |
|
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
|
紫外线、水暴露/浸泡 UV-light, water exposure/immersion UV light, water exposure/immersion |
UL 746C | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Tensile Bar |
| 3 0,20 in/min |
| 4 2,0 in/min |
| 5 类型 1, 2,0 in/min |
| 6 0,051 in/min |
| 7 0,079 in/min |
| 8 Yield |
| 9 0,49 in/min |
| 10 Break |
| 11 80*10*3 sp=62mm |
| 12 80*10*3 |
| 13 80*10*4 mm |
| 14 标准 B (120°C/h), 载荷2 (50N) |
|
【新闻资讯】查看全部
改性塑料硬度如何改良?
2017-03-22 硬度是指材料抵抗其它较硬物体压入其表面的能力，硬度值的大小是表征材料软硬程度的有条件的定量反映，它不是一个单纯而确定的物理量，那么改性塑料硬度怎么样?改性塑料硬度如何改进? 硬度值的大小不仅取决于材料的本身，而且取决于测试条件和测定方法，即不同的硬度测量方法，对同一种材料测定的硬度值不尽相同。因此，要比较材料之间的硬度大小，必须用同一种测量方法测量的硬度值，才有可比性。 常用于表示硬度的方法有如下几种： a、 邵氏硬度 b、 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付