牌号简介 About |
---|
LNP*Thermocomp*化合物DX13354X是一种可着色、玻璃纤维增强的聚碳酸酯树脂基材料溶液,具有稳定的电镀和射频性能,具有优异的刚度、良好的表面和良好的冲击强度。该产品可用于激光直接结构应用的内部和外部零件。 LNP* Thermocomp* compound DX13354X is a colorable, glass fiber reinforced Polycarbonate resin based LDS material solution with stable plating and RF performance, providing excellent stiffness with good surface and good impact strength. The product is available for internal and external parts for Laser Direct Structuring applications. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PC Polycarbonate
用途:激光直接成型;
加工条件:注射成型 Injection Molding
性能特点: 机械强度好; 冲击性能好; 表面光泽度好; Good Rigidity,Good surface appearance,High impact resistance
填料:玻璃纤维
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.43 | g/cm³ | ASTM D792, ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
280℃,2.16kg 280℃,2.16kg |
12 | g/10min | |
300℃,1.20kg 300℃,1.20kg |
16 | g/10min | |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
13.0 | cm³/10min | ASTM D1238 |
收缩率 Shrinkage rate |
内部方法 | ||
MD:3.2 mm MD:3.2 mm |
0.10 到 0.30 | % | |
TD:3.2 mm TD:3.2 mm |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 1 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture 2 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 3 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ASTM D790,ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/2C | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/2U | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ 4 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
23℃ 23℃ 5 |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 6 |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 7 |
℃ | ISO 75-2/Af | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电常数 Dielectric constant |
内部方法 | ||
1.10 GHz 1.10 GHz |
|||
1.9 GHz 1.9 GHz |
|||
5.00 GHz 5.00 GHz |
|||
耗散因数 Dissipation factor |
内部方法 | ||
1.1 GHz 1.1 GHz |
|||
1.9 GHz 1.9 GHz |
|||
5 GHz 5 GHz |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 类型 1, 0.20 in/min |
4 80*10*4 |
5 80*10*4 mm |
【新闻资讯】查看全部 ![]()
我国科学家研制出有望替代塑料的仿生新材料
2020-11-16 搜料网资讯: 塑料制品给现代生活带来便利,也造成环境污染。近期,中国科学技术大学俞书宏院士团队使用定向变形组装方法,研制出具有仿生结构的高性能材料,具有比石油基塑料 |
我国科学家研制出有望替代塑料的仿生新材料 搜料网资讯:塑料制品给现代生活带来便利,也造成环境污染。近期,中国科学技术大学俞书宏院士团队使用“定向变形组装”方法,研制出具有仿生结构的高性能材料,具有比石油基塑料更好的机械与热性能,有望成为其替代品。
目前,大多数塑料来自石油产品,废弃后难以降解,造成持续性的环境污染问题。同时,现有的生物基材料存在成本高或难制造等问题,制约了推广应用。 近期,中国科学技术大学俞书宏院士团队运用仿生结构设计理念,发展出一种被称为“定向变形组装”的新材料制造方法,将纤维素纳米纤维和二氧化钛包覆的云母片复合,制备出具有仿生结构的高性能可持续结构材料。 这种新材料采用仿珍珠母的结构设计,实验表明,它既具有远高于工程塑料的强度,又有很强的韧性和抗裂纹扩展性能。在零下130摄氏度至零上150摄氏度的温度范围内,其尺寸几乎没有变化,与塑料的剧烈收缩和膨胀形成鲜明对比。在室温下,它的热膨胀系数仅为大多数塑料的约十分之一。 日前,国际知名学术期刊《自然·通讯》发表了这项研究成果。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。