牌号简介 About |
---|
DAI-EL G-912 DAI-EL™ G-912是一种中等粘度的三元共聚物,适用于各种过氧化物固化系统。可以配制G-912以消除后固化过程。G-912设计用于需要优良耐化学、蒸汽和压缩永久变形的传递和压缩成型应用。DAI-EL G-912 DAI-EL™ G-912是一种含氟弹性体,由偏二氟乙烯/四氟乙烯/六氟丙烯三元共聚物组成。这种材料可以用过氧化物固化。该材料具有最高氟含量等级,与多元醇固化系列相比具有优异的机械性能、耐酸性、耐蒸汽性和耐化学性以及良好的压缩永久性。 DAI-EL® G-912 DAI-EL® G-912 is a medium viscosity terpolymer suitable for various peroxide cure systems. DAI-EL® G-912 can be formulated to eliminate the post cure process. DAI-EL® G-912 is designed for transfer and compression molding applications that require excellent chemical, steam and compression set resistance. DAI-EL® G-912 DAI-EL G-912 is a fluoroelastomer comprising terpolymer of vinylidenefluoride/tetrafluoroethylene/hexafluoropropylene. This material can be cured by peroxide. This material is of the grade of the highest fluorine content and provides excellent mechanical properties, acid, steam and chemical resistance and good compression set properties in comparison to the polyol cure series. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.87 到 1.91 | g/cm³ | |
门尼粘度 Mooney viscosity |
|||
ML 1+10,121℃ ML 1+10,121℃ |
56 | MU | |
氟含量 Fluorine content |
71 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,25℃ Shore A, 25 ℃ |
73 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,25℃ Yield, 25 ℃ |
20.0 | MPa | |
100% 应变,25℃ 100% strain, 25 ℃ |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂,25℃ Fracture, 25 ℃ |
% | ||
撕裂强度 tear strength |
|||
25℃ 25℃ |
kN/m | ||
压缩形变 Compression deformation |
|||
25℃,70 hr 25℃,70 hr |
% | ||
100℃,70 hr 100℃,70 hr |
% | ||
175℃,70 hr 175℃,70 hr |
% | ||
200℃,70 hr 200℃,70 hr |
% | ||
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
|||
230℃,70 hr 230℃,70 hr |
% | ||
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
|||
230℃,70 hr 230℃,70 hr |
% | ||
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
|||
邵氏 A,230℃,70 hr Shore A, 230 ℃, 70 hr |
|||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化温度 curing temperature |
℃ | ||
固化时间 Curing time |
|||
Curelastmeter Curelastmeter |
min | ||
Gehman Torsion Test Gehman Torsion Test |
|||
T10 T10 |
℃ | ||
T2 T2 |
℃ | ||
TR Test TR Test |
|||
TR10 TR10 |
℃ | ||
TR70 TR70 |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 23°C |
3 25% compression |
【新闻资讯】查看全部
中国石化斥资逾70亿元收购PBT、PBAT等业务
2021-12-06 搜料网资讯: (1)中国石化拟以44.3亿元购买中国石化集团资产经营管理有限公司的生产经营性业务的股权类资产、非股权类资产及负债; (2)下属全资子公司仪征化纤拟以11.4亿元购 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |