D/W 224是一种经过刮削、拉伸的聚四氟乙烯,已在两侧蚀刻了钠萘,以便在复合结构软管和类似产品中与自身和其他基材粘合。拉伸过程产生的薄膜具有显著增强的拉伸性能。D/W 224正在液压、化学和其他需要与弹性材料进行内部粘合的软管结构中寻找应用。 D/W 224 is a skived, tensilzed PTFE that has been sodium napthalene etched on both sides to allow bonding to itself and other substrates within composite construction hoses and similar products. The tensilzing process yields as film with significantly enhanced tensile properties. D/W 224 is finding applications in hydraulic, chemical and other hose constructions where internal bonding to the elastomeric materials is required. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Thickness Thickness |
50.8 到 127 | nm | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
MD,屈服 MD, yield |
124 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
|||
MD,断裂 MD, fracture |
100 | % | ASTM D882 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
连续使用温度 Continuous use temperature |
260 | ℃ | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
160 | kV/mm | ASTM D149 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Core ID Core ID |
cm | ||
Maximum Roll OD Maximum Roll OD |
mm | ||
Width Width |
mm |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
菲亚特与索尔维合作推出首个碳纤维汽车转向节
2021-06-04 搜料网资讯: 菲亚特集团成员企业玛涅蒂马瑞利公司(Magneti Marelli,以下简称为MM)与热塑性塑料供应商索尔维合作,推出首个 碳纤维 汽车转向节。 汽车转向节也叫轮毂架或悬架立柱 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |