牌号简介 About |
---|
20纤维纺丝用均聚物聚丙烯1517采用Unipol-PP技术,采用气相流化床反应器,采用高活性催化剂体系,以保证物理性能和批次间的一致性。本产品适用于纤维纺纱和其他关键挤压应用。1517产品提供:优良的颜色和加工稳定性,优良的纤维纺纱特性,抗气体褪色,增强的纤维弹性,优良的批量一致性,Pinnacle's 1517聚丙烯,由Pinnacle聚合物公司销售,天然的,未着色的颗粒形式符合CFR标题的适当要求。21,第177部分,B子部分,第177.1520(c)1.1a.节可用于与第176.170(c)节表1中所述的食品类型I、II、IV-B、VII-B和VIII接触,在第176.170(c)节表2中所述的B至H条件下使用,以及与第176.170(c)节表1中所述的食品类型III、IV-A、V、VI、VII-A和IX接触。第176.170(c)节表2中所述的D至H用途。 20 MELT FLOW HOMOPOLYMER FOR FIBER SPINNING Pinnacle Polymers Polypropylene 1517 is made via UNIPOL™ PP technology, which utilizes gas-phase fluidized bed reactors with a high activity catalyst system to ensure uniform physical properties and lot-to-lot consistency. This product is intended for fiber spinning and other critical extrusion applications. The 1517 product provides: Excellent color and processing stability Superior fiber spinning characteristics Resistance to gas fading Enhanced fiber resiliency Excellent lot-to-lot consistency Pinnacle's 1517 polypropylene as marketed by Pinnacle Polymers Company, in natural, uncolored pellet form complies with appropriate requirements of CFR Title 21, Part 177, Subpart B, Section 177.1520 (c) 1.1a. May be used in contact with food types I, II, IV-B, VII-B and VIII described in Table 1 of section 176.170(c), under conditions of use B through H described in table 2 of section 176.170(c) and with food types III, IV-A, V, VI, VII-A, and IX described in Table 1 of section 176.170(c) under conditions of use D through H described in table 2 of section 176.170(c). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
20 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
1.4 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding 2 |
34.5 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding 2 |
9.0 | % | ASTM D638 |
弯曲模量 Bending modulus 3 |
|||
1% 正割,3.20 mm,注塑成型 1% cut, 3.20 mm, injection molded 3 |
MPa | ASTM D790-A | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 4 |
|||
23℃,3.2mm,注塑成型 23 ℃, 3.2mm, injection molding 4 |
kJ/m² | ASTM D256 | |
23℃,3.2mm,注塑成型 23 ℃, 3.2mm, injection molding 4 |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 2.0 in/min |
3 类型 1, 0.050 in/min |
4 Type I |
【新闻资讯】查看全部
中维化纤年产8万吨尼龙66工业品项目开工
2022-05-12 5月6日,在河南特种尼龙小镇工品园区举行年产8万吨尼龙66工业品项目开工仪式 。 杨建强是 县委书记,他 在致辞中指出,近年来,淇县深入贯彻落实省委、省政府优势再造、换道领跑 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |