牌号简介 About |
---|
Moplen HP400H Moplen HP400H是挤出应用的均聚物。Moplen HP400H在环境温度下表现出易加工性和良好的刚度/冲击平衡。Moplen HP400H的主要应用是热成型的浴缸和容器,中拉托盘和泡罩包装,花盆和小型挤压吹塑瓶。适用于配制。通用均聚聚丙烯,用于挤出和瓶子成型。典型应用包括挤压带、吸管、缩微胶片、绳索、文具纸和吹塑瓶。MOPLEN HP400H通用聚丙烯均聚物树脂特点:良好的加工性、低气味和味道传递、优异的耐化学性、低黄度、良好的拉伸强度应用:狭缝带吸管单丝。绳索、绳线固定板、瓶子、烧瓶 Moplen HP400H Moplen HP400H is a homopolymer for extrusion and compounding applications. Moplen HP400H exhibits easy processability and a good stiffness/impact balance at ambient temperature. It is typically used by customers in applications such as: thermoformed tubs, containers, medium draw trays and blister packs, flowerpots and small extrusion blow moulded bottles. Moplen HP400H General Purpose Polypropylene Homopolymer Resin Features: Good processability Low odor and taste transfer Excellent chemical resistance Low yellowness Good tensile strength Applications: Slit tape Straw Monofilaments Rope, twine Stationary sheets Bottles, flasks |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ASTM D792 , ISO 1183/D |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
2.1 | g/10min | ASTM D1238 |
230℃,2.16kg 230℃,2.16kg |
2.0 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
|||
230℃,2.16 kg 230℃,2.16 kg |
2.70 | cm³/10min | ISO 1133 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
4.0 | kJ/m² | ISO 179/1eA |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
0℃ 0℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60° 60° |
ASTM D2457 | ||
雾度 Haze |
|||
1000 µm 1000 µm |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
球压硬度 Ball hardness |
|||
H358/30 H358/30 |
MPa | ISO 2039-1 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ASTM D638 , ISO 527-2 | |
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
“炼化+乙烯+新材料”共同发力!恒力石化上半年净利86.42亿元
2021-08-18 搜料网资讯: 8月16日晚间,恒力石化披露2021年半年度报告,公司2021年上半年实现营业收入1045.74亿元,同比增长55.25%;净利润86.42亿元,同比增长56.65%;基本每股收益1.23元。 炼化+乙烯 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |