牌号简介 About |
---|
陶氏制造的TYRIL™ 苯乙烯-丙烯腈 (SAN) 树脂具有优异的耐化学品性能、强度、硬度和尺寸稳定性,适用产品范围广阔。TYRIL 867的主要特征是其物理性能之间优异的平衡性。TYRIL 867 E 专用于要求加工性能好、耐化学品性能好和耐热性能好以及强度很高的应用领域。加入了紫外线稳定剂的牌号产品具有优异的耐候性能,特别适宜于挤出片材和热成型加工。 应用领域: 小型电器:透明的厨房电器零部件 用于淋浴房、灯光散射器的挤出片材 家用器具:食品储存容器 卫浴配件:肥皂盒,马桶盖 TYRIL* styrene-acrylonitrile (SAN) resins are designed to offer superior chemical resistance, strength, hardness and dimensional stability in a broad range of product applications. The key property of TYRIL 867 E is excellent balance of physical properties. TYRIL 867 E is specifically designed to provide good processability, good chemical and heat resistance and very good strength. The UV-stabilized version exhibits excellent weather ability, suitable in particular for extruded sheet and thermoforming applications. Applications: Extruded sheet for shower cabinets, or glazing Sanitary accessories: soap dishes, toilet seats |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.08 | g/cm³ | ASTM D792 |
密度 Density |
1.08 | g/cm³ | ISO 1183/B |
密度 Density |
1.08 | g/cm³ | ISO 1183-2 |
表观密度 Apparent density |
0.69 | g/cm³ | ASTM D1895 |
表观密度 Apparent density |
0.69 | g/cm³ | ISO 60 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
220℃,10.0kg 220℃,10.0kg |
g/10min | ASTM D1238 | |
230℃,3.80kg 230℃,3.80kg |
g/10min | ASTM D1238 | |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
220℃,10.0kg 220℃,10.0kg |
g/10min | ISO 1133 | |
230℃,3.80kg 230℃,3.80kg |
g/10min | ISO 1133 | |
熔体体积流动速率 Melt Volume Rate |
|||
220℃,10 kg 220℃,10 kg |
cm³/10min | ISO 1133 | |
吸水率 Water absorption rate |
|||
饱和 saturated |
% | ISO 62-2 | |
平衡 balance |
% | ISO 62-2 | |
粘度值 Viscosity value |
cm³/g | ISO 307, 1157, 1628 2 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁冲击强度 Charpy impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU 2 | |
-30℃ -30℃ |
kJ/m² | ISO 179/1eU 2 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
kJ/m² | ISO 180 | |
拉伸缺口冲击强度 Tensile Notch Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 8256/1 2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 2 | |
-- -- |
℃ | ASTM D1525 4 | |
-- -- |
℃ | ASTM D1525 5 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
1/℃ | ISO 11359-2 2 | |
MD MD |
1/℃ | ISO 11359-2 2 | |
MD MD |
1/℃ | DIN 53752 | |
比热 specific heat |
J/kg/℃ | ASTM D2766 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 2 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 2 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
|||
100 Hz 100 Hz |
IEC 60250 2 | ||
1 MHz 1 MHz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 2 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
IEC 60250 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm 6 |
UL 94 | ||
阻燃等级 Flame retardant level |
|||
1.60 mm 1.60 mm |
ISO 1210 2 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/5 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2 2 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2 2 | |
Nominal strain at break Nominal strain at break |
% | ISO 527-2 2 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 | ||
M 级 M-level |
ISO 2039-2 | ||
特殊值 |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
-- -- |
℃ | ISO 306/A120 | |
B50 B50 |
℃ | ISO 306 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
3 0.20 in/min |
4 标准 B (120°C/h), 压 力1 (10N) |
5 速率 A (50°C/h), 载荷2 (50N) |
6 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
【新闻资讯】查看全部
慎用一次性塑料制品打包剩饭剩菜
2017-08-29 我们一天接触到塑料的频率越来越高,塑料制品已经融入到我们的生活当中。一次性塑料制品餐具被广泛运用在食品包装当中。那么这些一次性塑料餐具真的安全吗? 据调查显示,保鲜膜、保鲜袋与水或酸性食物接触时比较安全, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |