牌号简介 About |
---|
Vydyne® 21SPF BLK是一种通用的PA66树脂。可提供黑色,主要设计用于注塑加工。该等级提供了高强度、刚性、韧性好、熔点高、表面润滑性好、耐磨性和耐多种化学品、机器和机油、溶剂和汽油等工程性能的良好平衡组合。Vydyne® 21SPF BLK树脂允许生产具有良好初始颜色和良好性能和使用再研磨时保持颜色的成型零件。该树脂经保险商实验室认可,符合许多工业、联邦和军用优质通用PA66树脂规范的要求。Vydyne® 21SPF BLK树脂是内部和外部润滑,以改善机器饲料和特殊的模具释放。它用于高生产率的应用。在许多应用中,由于零件可能在较高温度下从型腔中取出,因此可以缩短成型周期。在零件容易粘在型腔中的困难模具中,Vydyne® 21SPF BLK可以减少或消除模具释放喷剂的需要。在常规生产基础上实施较短的成型周期之前,应根据规范检查关键的成型零件尺寸。 Vydyne 21SPF BLK is a general-purpose PA66 resin. Available in black, it is designed principally for injection-molding fabrication. This grades offer a well-balanced combination of engineering properties characterized by high strength; rigidity; good toughness; high melt point; good surface lubricity; abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline. Vydyne 21SPF BLK resin permits production of molded parts with good initial color plus good property and color retention when using regrind. This resin is recognized by Underwriters Laboratories and conforms to the requirements of many industrial, federal and military specifications for premium-quality, general-purpose PA66 resins. Vydyne 21SPF BLK resin is internally and externally lubricated for improved machine feed and exceptional mold release. It is intended for use in high-productivity applications. In many applications, the molding cycle can be reduced because parts may be removed from the cavity at higher temperatures. In difficult molds where parts have a tendency to stick in the cavity, Vydyne 21SPF BLK can reduce or eliminate the need for mold release sprays. Critical molded part dimensions should be checked against specifications before implementing shorter molding cycles on a routine production basis. |
产品描述 Product Description
厂家:美国奥升德 Ascend
类别:PA66 PA66
用途:轴承;电器外壳;工业应用;连接器;衬套;凸轮;
颜色:黑色
加工条件:注射成型 Injection Molding
性能特点: 耐磨; 机械强度好; 耐油; 含脱模剂; 耐汽油; 成型周期快; 耐化学性; 防火阻燃等级V-2; 润滑性; 韧性好; Good Rigidity,Good flexibility,Quick molding cycle,Good stripping performance,Lubricating,Good wear resistance,Grease resistance,Solvent resistance,Gasoline resistance,V-2
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.14 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:23℃,2.0 mm TD:23℃,2.0 mm |
2.0 | % | ISO 294-4 |
MD:23℃,2.0 mm MD:23℃,2.0 mm |
2.0 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
2.4 | % | ISO 62 |
23℃,24hr 23℃,24hr |
1.2 | % | ISO 62 |
耐候性 Weathering resistance |
UL 746C | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
泊松比 Poisson's ratio |
ISO 527-2 | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180 | ||
-30℃ -30℃ |
kJ/m² | ISO 180 | |
23℃ 23℃ |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃,2 mm TD:23~55℃,2 mm |
1/℃ | ISO 11359-2 | |
MD:23~55℃,2 mm MD:23~55℃,2 mm |
1/℃ | ISO 11359-2 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
UL 746 | ||
0.40 mm 0.40 mm |
℃ | UL 746 | |
0.71 mm 0.71 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
0.40 mm 0.40 mm |
℃ | UL 746 | |
0.71 mm 0.71 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
0.40 mm 0.40 mm |
℃ | UL 746 | |
0.71 mm 0.71 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
0.75 mm 0.75 mm |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
1 mm 1 mm |
kV/mm | IEC 60243 | |
耐电弧性 Arc resistance |
|||
3.0 mm 3.0 mm |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
3.00 mm 3.00 mm |
V | IEC 60112 | |
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
0.40 mm 0.40 mm |
UL 746 | ||
0.71 mm 0.71 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
0.40 mm 0.40 mm |
UL 746 | ||
0.71 mm 0.71 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.40 mm 0.40 mm |
UL 94 | ||
0.71 mm 0.71 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.40 mm 0.40 mm |
℃ | IEC 60695-2-12 | |
0.71 mm 0.71 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.4 mm 0.4 mm |
℃ | IEC 60695-2-13 | |
0.71 mm 0.71 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
美国华盛顿州立大学研发高效回收碳纤维技术
2017-05-04 据美国华盛顿州立大学消息,该校机械与材料工程学院教授Jinwen Zhang领导的科研小组最近研究出一种碳纤维回收新技术。 美国华盛顿州立大学研发高效回收碳纤维技术 |
美国华盛顿州立大学研发高效回收碳纤维技术 据美国华盛顿莱斯大学信息,该学校机械设备与原材料工程学校专家教授Jinwen Zhang领导干部的科学研究工作组近期科学研究出一种碳纤维收购 新技术应用。 美国华盛顿莱斯大学产品研发高效率收购 碳纤维技术性 该精英团队用弱酸性做为催化剂,利用含该催化剂的液体酒精在相对性超低温下对热固性塑料原材料开展溶解。为获得更强的溶解实际效果,科学研究工作人员在试验全过程中对原材料开展提温,使带有催化剂的液體可以更强的渗入高分子材料內部,破坏在其中早已干固的繁杂构造。Zhang专家教授利用酒精使树脂产生澎涨,再用氯化镁破坏化学分子中的碳氮键。 “要想完成碳纤维的合理收购 ,关键所在寻找可以合理渗入早已干固的树脂系统软件而且破坏其离子键的催化剂。”张教授表明说。 该方式已被试验证实合理,溶解以后的碳纤维和树脂被各自储存,并资金投入在生产。该精英团队早已为其申请办理了技术性专利权,并尝试资金投入商业化的运用。 该科学研究受航空公司技术革新联合中心(JCATI)支助,参加者还包含副教授职称Junna Xin,博士研究生Tuan Liu及其研究生Xiaolong Guo。 来源于:中国全球高分子材料展会 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。