牌号简介 About |
---|
Vibrathane B625是一种以聚醚为基础的MDI端接预聚物,当用二醇固化时,可得到60A到95A硬度的聚氨酯。Vibrathane B 625具有极低的粘度,来自它的聚氨酯具有优良的低温性能。高耐磨性,特别是抗冲击性。出色的水解稳定性。高弹性。 VIBRATHANE B625 is a polyether-based MDI-terminated prepolymer which yields 60A to 95A hardness urethanes when cured with diols. Vibrathane B 625 is characterized by exceptionally low viscosity and urethanes from it have: Excellent low-temperature properties. High abrasion resistance, especially to impingement. Outstanding hydrolytic stability. High resilience. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ASTM D792 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
60 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
15.9 | MPa | ASTM D412 |
100% 应变 100% strain |
1.72 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
600 | % | ASTM D412 |
撕裂强度 tear strength |
|||
开裂 cracking |
kN/m | ASTM D470 | |
压缩形变 Compression deformation |
|||
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
|||
110℃ 110℃ |
hr | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
储存稳定性 storage stability |
min | ||
后固化时间 Post curing time |
|||
110℃ 110℃ |
hr |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
实现长链二元酸绿色制造——记石化绿色工艺之生物法制备长链二元酸
2021-08-09 搜料网资讯: 长链二元酸通常可以采用化学法或生物法来生产,传统上以化学法生产为主。但传统化学法自2015年底开始逐步退出市场,以生物制造方法生产的长链二元酸系列产品由于经 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |