MVR(300°C/1.2 kg)8.0 cm³/10 min;20%玻璃纤维增强;阻燃;UL 94V-0/1.5 mm;中等粘度;易释放;注射成型-熔融温度310-330°C;仅提供不透明颜色 MVR (300 °C/1.2 kg) 8.0 cm³/10 min; 20 % glass fiber reinforced; flame retardant; UL 94V-0/1.5 mm; medium viscosity; easy release; injection molding - melt temperature 310 - 330 °C; available in opaque colors only |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.34 | g/cm³ | ISO 1183 |
表观密度 Apparent density 2 |
0.64 | g/cm³ | ISO 60 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
10 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
8.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD TD |
0.30 to 0.50 | % | ISO 2577 |
MD MD |
% | ISO 2577 | |
TD:2.0 mm TD:2.0 mm 3 |
% | ISO 294-4 | |
MD:2.0 mm MD:2.0 mm 3 |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 6 |
|||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 179/1eU | |
23℃,完全断裂 23 ℃, completely fractured |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 7 |
|||
23℃,完全断裂 23 ℃, completely fractured 7 |
kJ/m² | ISO 7391 | |
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
ISO 6603-2 | ||
-30℃ -30℃ |
J | ISO 6603-2 | |
23℃ 23℃ |
J | ISO 6603-2 | |
多轴向仪器化冲击力峰值 Multi axial instrumented peak impact force |
ISO 6603-2 | ||
-30℃ -30℃ |
N | ISO 6603-2 | |
23℃ 23℃ |
N | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
136℃ 136℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient 8 |
|||
23℃ 23℃ 8 |
W/m/K | ISO 8302 | |
相对温度指数 Relative temperature index |
|||
电气性能,1.50 mm Electrical performance, 1.50 mm |
℃ | UL 746 | |
强度机械性能,1.50 mm Strength mechanical performance, 1.50 mm |
℃ | UL 746 | |
冲击机械性能,1.50 mm Impact mechanical performance, 1.50 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
IEC 60112 | ||
解决方案 A Solution A |
V | IEC 60112 | |
解决方案 B Solution B |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.36 mm 0.36 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index 9 |
% | ISO 4589-2 | |
小型燃烧器火焰的应用 The Application of Small Burner Flames |
|||
2.00 mm 2.00 mm |
DIN 4102 | ||
Method K and F:2.00 mm Method K and F:2.00 mm |
DIN 53438-1, -3 | ||
燃烧速率 Burning rate |
|||
USFMVSS,> 1.00 mm USFMVSS,> 1.00 mm |
ISO 3795 | ||
Flash Ignition Temperature Flash Ignition Temperature |
℃ | ASTM D1929 | |
针焰测试 Needle flame test |
IEC 60695-11-5 | ||
Method F:1.50 mm Method F:1.50 mm |
min | IEC 60695-11-5 | |
Method F:2.00 mm Method F:2.00 mm |
min | IEC 60695-11-5 | |
Method F:3.00 mm Method F:3.00 mm |
min | IEC 60695-11-5 | |
Method K:1.50 mm Method K:1.50 mm |
min | IEC 60695-11-5 | |
Method K:2.00 mm Method K:2.00 mm |
min | IEC 60695-11-5 | |
Method K:3.00 mm Method K:3.00 mm |
min | IEC 60695-11-5 | |
自燃温度 Autoignition temperature |
℃ | ASTM D1929 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
电解腐蚀 Electrolytic corrosion |
|||
23℃ 23℃ |
IEC 60426 | ||
ISO Shortname ISO Shortname |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus 4 |
|||
23℃ 23℃ 4 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
|||
23℃ 23℃ 4 |
MPa | ISO 178 | |
弯曲应变 Bending strain 5 |
% | ISO 178 | |
球压硬度 Ball hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Pellets |
3 60x60x2 mm, 500 bar |
4 0,079 in/min |
5 2 mm/min |
6 Based on ISO 179-1eA, 3 mm |
7 Based on ISO 180-A, 3 mm |
8 Cross-flow |
9 程序 A |
【新闻资讯】查看全部
上海市质监局抽查食品用塑料包装复合袋
2017-12-13 从上海市质量技术监督局官网获悉,该局近期组织相关质检机构对上海市生产的食品用塑料包装复合膜(袋)产品质量进行了监督抽查。共计抽查产品60批次,经检验,1批次产品不合格。 据上海市质量技术监督局介绍,食品用塑料包装复合膜(袋)是列入食品相关产品生产许可发证目录的产品。上海市共有食品用塑料复合膜(袋)生产企业68家,本次计划抽查68家,实际抽到产品的有58家企业,另有10家企业由于停产未抽到样品。 本次监督抽查依据GB/T10004-2008《包装用塑料复合膜、 |
上海市质监局抽查食品用塑料包装复合袋 从上海质监局官方网站获知,各地各部门最近机构有关质量检验组织 对上海生产制造的食品用塑料包装复合膜(袋)产品品质开展了监管抽查。总共抽查商品60批号,经检测,1批号商品不过关。 据上海质监局详细介绍,食品用塑料包装复合膜(袋)是纳入食品相关产品生产许可证颁证文件目录的商品。上海现有食品用塑料复合膜(袋)制造业企业68家,此次方案抽查68家,具体抽中商品的有58家公司,另有10家公司因为停工未抽中试品。 此次监管抽查根据GB/T10004-2008《包装用塑料复合膜、袋 干法复合、挤出复合》、GB/T18192-2008《液体食品无菌包装用纸基复合材料》、GB18454-2001《液体食品无菌包装用复合袋》、GB/T18706-2008《液体食品保鲜包装用纸基复合材料》、GB19741-2005《液体食品包装用塑料复合膜、袋》、QB/T1871-1993《双向拉伸尼龙(BOPA)/低密度聚乙烯(LDPE)复合膜、袋》、GB/T28118-2011《食品包装用塑料与铝箔复合膜、袋》、GB/T28117-2011《食品包装用多层共挤膜、袋》、GB4806.7-2016《食品安全国家标准 食品接触用塑料材料及制品》等规范规定,对食品用塑料包装复合膜(袋)商品的以下新项目开展了检验:扯断力、抗拉强度、拉伸强度/破裂允差应变力、脱离力、钉合抗压强度、抗钟摆冲击性能、co2通过量、水蒸汽通过量、感观指标值、蒸发残渣、总转移量、高锰酸钾溶液使用量、重金属超标(以PB计)、褪色实验、有机溶剂含量及总产量、苯类有机溶剂含量、甲苯二胺等。 数据显示,上海市春成包裝彩色印刷有限责任公司生产制造 (允差)的1批号食品用塑料包装复合包装袋(PET/CPP)(型号规格:mm:230×135×0.062;出厂日期/生产批号:2017-04-24)试品,被验出有机溶剂含量总产量新项目不过关。 来源于:中国质量新闻 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。