牌号简介 About |
---|
DAI-EL G-901 DAI-EL™ G-901是一种适用于各种过氧化物固化系统的三元共聚物。可配制G-901以消除后固化过程。G-901适用于需要优良耐化学性和蒸汽性的转移和压缩成型应用。DAI-EL G-901 DAI-EL™ G-901是一种含氟弹性体,由偏二氟乙烯/四氟乙烯/六氟丙烯三元共聚物组成。这种材料可以用过氧化物固化,具有最高的氟含量等级,并提供良好的机械性能,与多元醇固化系列相比具有耐酸、耐蒸汽和耐化学性。 DAI-EL® G-901 DAI-EL® G-901 is a terpolymer suitable for various peroxide cure systems. DAI-EL® G-901 can be formulated to eliminate the post cure process.DAI-EL® G-901 is suitable for transfer and compression molding applications requiring excellent chemical and steam resistance. DAI-EL® G-901 DAI-EL G-901 is a fluoroelastomer comprising terpolymer of vinylidenefluoride/tetrafluoroethylene/hexafluoropropylene. This material can be cured by peroxide, is of the highest fluorine content grade and provides excellent mechanical properties, and acid, steam and chemical resistance in comparison to polyol cure series. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.87 到 1.91 | g/cm³ | |
门尼粘度 Mooney viscosity |
|||
ML 1+10,121℃ ML 1+10,121℃ |
48 | MU | |
氟含量 Fluorine content |
71 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,25℃ Shore A, 25 ℃ |
70 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,25℃ Yield, 25 ℃ |
22.0 | MPa | |
100% 应变,25℃ 100% strain, 25 ℃ |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂,25℃ Fracture, 25 ℃ |
% | ||
撕裂强度 tear strength |
|||
25℃ 25℃ |
kN/m | ||
压缩形变 Compression deformation |
|||
25℃,70 hr 25℃,70 hr |
% | ||
100℃,70 hr 100℃,70 hr |
% | ||
175℃,70 hr 175℃,70 hr |
% | ||
200℃,70 hr 200℃,70 hr |
% | ||
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
|||
230℃,70 hr 230℃,70 hr |
% | ||
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
|||
230℃,70 hr 230℃,70 hr |
% | ||
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
|||
邵氏 A,230℃,70 hr Shore A, 230 ℃, 70 hr |
|||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化温度 curing temperature |
℃ | ||
固化时间 Curing time |
|||
Curelastmeter Curelastmeter |
min | ||
Gehman Torsion Test Gehman Torsion Test |
|||
T10 T10 |
℃ | ||
T2 T2 |
℃ | ||
TR Test TR Test |
|||
TR10 TR10 |
℃ | ||
TR70 TR70 |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 23°C |
3 25% compression |
【新闻资讯】查看全部
避险情绪升温 在岸人民币汇率跌逾200点
2021-07-28 搜料网资讯: 昨日,此前横盘整理多日的人民币汇率盘中大幅下挫,创下4月以来新低。截至27日下午收盘,在岸人民币日内跌逾200点,最低触及6.5133;离岸人民币连续跌破6.49、6.50、6 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |