牌号简介 About |
---|
Texin® 245树脂是一种芳香族聚酯基热塑性聚氨酯,肖氏硬度约为43d,可通过注塑加工,不建议采用挤出工艺。 Texin 245 resin is an aromatic polyester-based thermoplastic polyurethane with a Shore hardness of approximately 43D. It can be processed by injection molding; extrusion processes are not recommended. |
产品描述 Product Description
厂家:德国科思创 Covestro
类别:TPU-酯 TPU-酯
用途:齿轮;车轮;
加工条件:注射成型 Injection Molding
性能特点: 防火阻燃等级HB; 耐磨; 耐油; 耐低温; 冲击性能好; 韧性好; 耐燃油; Good flexibility,High impact resistance,Antifreeze,Good wear resistance,Grease resistance,Fuel resistance,HB
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.21 | g/cm³ | ASTM D792 |
密度 Density |
1.21 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 2577 | ||
TD:2.54 mm TD:2.54 mm |
0.80 | % | ASTM D955 |
MD:2.54 mm MD:2.54 mm |
0.80 | % | ASTM D955 |
TD:2.54 mm TD:2.54 mm |
0.80 | % | ISO 2577 |
MD:2.54 mm MD:2.54 mm |
% | ISO 2577 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
邵氏 D Shaw's D |
ISO 868 | ||
弯曲模量 Bending modulus |
ASTM D790 | ||
23℃ 23℃ |
MPa | ASTM D790 | |
70℃ 70℃ |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
70℃ 70℃ |
MPa | ISO 178 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ISO 4649 | |
1000 周期,1000 g,H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ASTM D1044 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D412 | |
屈服 yield |
MPa | ISO 37 | |
300% 应变 300% strain |
MPa | ASTM D412 | |
300% 应变 300% strain |
MPa | ISO 37 | |
100% 应变 100% strain |
MPa | ISO 37 | |
100% 应变 100% strain |
MPa | ASTM D412 | |
50% 应变 50% strain |
MPa | ISO 37 | |
50% 应变 50% strain |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 37 | |
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength 2 |
kN/m | ASTM D624 | |
撕裂强度 tear strength |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation |
ASTM D395B | ||
23℃,22 hr 23℃,22 hr 3 |
% | ASTM D395B | |
23℃,22 hr 23℃,22 hr |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr 3 |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
100℃,22 hr 100℃,22 hr 3 |
% | ASTM D395B | |
100℃,22 hr 100℃,22 hr |
% | ASTM D395B | |
压缩形变 Compression deformation |
ISO 815 | ||
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
23℃,22 hr 23℃,22 hr 3 |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr 3 |
% | ISO 815 | |
100℃,22 hr 100℃,22 hr |
% | ISO 815 | |
100℃,22 hr 100℃,22 hr 3 |
% | ISO 815 | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃,3.2mm -30℃,3.2mm |
J/m | ASTM D256 | |
23℃,3.2mm 23℃,3.2mm |
ASTM D256 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
脆化温度 Embrittlement temperature |
℃ | ISO 974 | |
玻璃化转变温度 Glass transition temperature |
℃ | DMA | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/50 | |
相对温度指数 Relative temperature index |
|||
电气性能,1.50 mm Electrical performance, 1.50 mm |
℃ | UL 746 | |
强度机械性能,1.50 mm Strength mechanical performance, 1.50 mm |
℃ | UL 746 | |
冲击机械性能,1.50 mm Impact mechanical performance, 1.50 mm |
℃ | UL 746 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ASTM D573 | ||
100℃,70 hr 100℃,70 hr |
% | ASTM D573 | |
100% Strain,100℃,70 hr 100% Strain,100℃,70 hr |
% | ASTM D573 | |
300% Strain,100℃,70 hr 300% Strain,100℃,70 hr |
% | ASTM D573 | |
100℃,168 hr 100℃,168 hr |
% | ASTM D573 | |
100% Strain,100℃,168 hr 100% Strain,100℃,168 hr |
% | ASTM D573 | |
300% Strain,100℃,168 hr 300% Strain,100℃,168 hr |
% | ASTM D573 | |
100℃,336 hr 100℃,336 hr |
% | ASTM D573 | |
100% Strain,100℃,336 hr 100% Strain,100℃,336 hr |
% | ASTM D573 | |
300% Strain,100℃,336 hr 300% Strain,100℃,336 hr |
% | ASTM D573 | |
100℃,504 hr 100℃,504 hr |
% | ASTM D573 | |
100% Strain,100℃,504 hr 100% Strain,100℃,504 hr |
% | ASTM D573 | |
300% Strain,100℃,504 hr 300% Strain,100℃,504 hr |
% | ASTM D573 | |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ISO 216 | ||
100℃,70 hr 100℃,70 hr |
% | ISO 216 | |
100% Strain 100℃,70 hr 100% Strain 100℃,70 hr |
% | ISO 216 | |
300% Strain 100℃,70 hr 300% Strain 100℃,70 hr |
% | ISO 216 | |
100℃,168 hr 100℃,168 hr |
% | ISO 216 | |
100% Strain 100℃,168 hr 100% Strain 100℃,168 hr |
% | ISO 216 | |
300% Strain 100℃,168 hr 300% Strain 100℃,168 hr |
% | ISO 216 | |
100℃,336 hr 100℃,336 hr |
% | ISO 216 | |
100% Strain 100℃,336 hr 100% Strain 100℃,336 hr |
% | ISO 216 | |
300% Strain 100℃,336 hr 300% Strain 100℃,336 hr |
% | ISO 216 | |
100℃,504 hr 100℃,504 hr |
% | ISO 216 | |
100% Strain 100℃,504 hr 100% Strain 100℃,504 hr |
% | ISO 216 | |
300% Strain 100℃,504 hr 300% Strain 100℃,504 hr |
% | ISO 216 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
ASTM D573 | ||
100℃,70 hr 100℃,70 hr |
% | ASTM D573 | |
100℃,168 hr 100℃,168 hr |
% | ASTM D573 | |
100℃,336 hr 100℃,336 hr |
% | ASTM D573 | |
100℃,504 hr 100℃,504 hr |
% | ASTM D573 | |
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air |
ISO 216 | ||
100℃,70 hr 100℃,70 hr |
% | ISO 216 | |
100℃,168 hr 100℃,168 hr |
% | ISO 216 | |
100℃,336 hr 100℃,336 hr |
% | ISO 216 | |
100℃,504 hr 100℃,504 hr |
% | ISO 216 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
ASTM D573 | ||
邵氏 D,100℃,70 hr Shore D, 100 ℃, 70 hr |
ASTM D573 | ||
邵氏 D,100℃,168 hr Shore D, 100 ℃, 168 hr |
ASTM D573 | ||
邵氏 D,100℃,336 hr Shore D, 100 ℃, 336 hr |
ASTM D573 | ||
邵氏 D,100℃,504 hr Shore D, 100 ℃, 504 hr |
ASTM D573 | ||
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
ISO 216 | ||
邵氏 D,100℃,70 hr Shore D, 100 ℃, 70 hr |
ISO 216 | ||
邵氏 D,100℃,168 hr Shore D, 100 ℃, 168 hr |
ISO 216 | ||
邵氏 D,100℃,336 hr Shore D, 100 ℃, 336 hr |
ISO 216 | ||
邵氏 D,100℃,504 hr Shore D, 100 ℃, 504 hr |
ISO 216 | ||
拉伸强度的变化率 The rate of change in tensile strength |
ASTM D471 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ASTM D471 | |
100% Strain,23℃,70 hr,in Reference Fuel C 100% Strain,23℃,70 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,70 hr,in Reference Fuel C 300% Strain,23℃,70 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ASTM D471 | |
100% Strain,23℃,168 hr,in Reference Fuel C 100% Strain,23℃,168 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,168 hr,in Reference Fuel C 300% Strain,23℃,168 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
100% Strain,23℃,336 hr,in Reference Fuel C 100% Strain,23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,336 hr,in Reference Fuel C 300% Strain,23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100% Strain,23℃,504 hr,in Reference Fuel C 100% Strain,23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,504 hr,in Reference Fuel C 300% Strain,23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100% Strain,100℃,70 hr,in ASTM #1 Oil 100% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,70 hr,in ASTM #1 Oil 300% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100% Strain,100℃,70 hr,in ASTM #3 Oil 100% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,70 hr,in ASTM #3 Oil 300% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100% Strain,100℃,168 hr,in ASTM #1 Oil 100% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,168 hr,in ASTM #1 Oil 300% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100% Strain,100℃,168 hr,in ASTM #3 Oil 100% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,168 hr,in ASTM #3 Oil 300% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100% Strain,100℃,336 hr,in ASTM #1 Oil 100% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,336 hr,in ASTM #1 Oil 300% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100% Strain,100℃,336 hr,in ASTM #3 Oil 100% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,336 hr,in ASTM #3 Oil 300% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100% Strain,100℃,504 hr,in ASTM #1 Oil 100% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,504 hr,in ASTM #1 Oil 300% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100% Strain,100℃,504 hr,in ASTM #3 Oil 100% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,504 hr,in ASTM #3 Oil 300% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
拉伸强度的变化率 The rate of change in tensile strength |
ISO 175 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ISO 175 | |
100% Strain,23℃,70 hr,in Reference Fuel C 100% Strain,23℃,70 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,70 hr,in Reference Fuel C 300% Strain,23℃,70 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ISO 175 | |
100% Strain,23℃,168 hr,in Reference Fuel C 100% Strain,23℃,168 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,168 hr,in Reference Fuel C 300% Strain,23℃,168 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
100% Strain,23℃,336 hr,in Reference Fuel C 100% Strain,23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,336 hr,in Reference Fuel C 300% Strain,23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100% Strain,23℃,504 hr,in Reference Fuel C 100% Strain,23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,504 hr,in Reference Fuel C 300% Strain,23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ISO 175 | |
100% Strain,100℃,70 hr,in ASTM #1 Oil 100% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,70 hr,in ASTM #1 Oil 300% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
100% Strain,100℃,70 hr,in ASTM #3 Oil 100% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,70 hr,in ASTM #3 Oil 300% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100% Strain,100℃,168 hr,in ASTM #1 Oil 100% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,168 hr,in ASTM #1 Oil 300% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100% Strain,100℃,168 hr,in ASTM #3 Oil 100% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,168 hr,in ASTM #3 Oil 300% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100% Strain,100℃,336 hr,in ASTM #1 Oil 100% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,336 hr,in ASTM #1 Oil 300% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100% Strain,100℃,336 hr,in ASTM #3 Oil 100% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,336 hr,in ASTM #3 Oil 300% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100% Strain,100℃,504 hr,in ASTM #1 Oil 100% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,504 hr,in ASTM #1 Oil 300% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
100% Strain,100℃,504 hr,in ASTM #3 Oil 100% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,504 hr,in ASTM #3 Oil 300% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
极限伸长率的变化率 Change rate of ultimate elongation |
ASTM D471 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ASTM D471 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
断裂时拉伸应力变化 Changes in tensile stress during fracture |
ISO 175 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ISO 175 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ISO 175 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
邵氏硬度的变化率 The rate of change in Shore hardness 2 |
ASTM D471 | ||
邵氏 D,23℃,70 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 70 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,70 hr,在基准燃料C中 Shore D, 23°C, 70 hr, in Reference Fuel C |
ASTM D471 | ||
邵氏 D,23℃,168 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 168 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,168 hr,在基准燃料中 Shore D, 23 ℃, 168 hr, in reference fuel |
ASTM D471 | ||
邵氏 D,23℃,336 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 336 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,336 hr,在基准燃料C中 Shore D, 23 ℃, 336 hr, in reference fuel C |
ASTM D471 | ||
邵氏 D,23℃,504 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 504 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,504 hr,,在基准燃料C中 Shore D, 23 ℃, 504 hr, in reference fuel C |
ASTM D471 | ||
邵氏 D,100℃,70 hr,在ASTM #1油中 Shore D, 100°C, 70 hr, in ASTM #1 Oil |
ASTM D471 | ||
邵氏 D,100℃,70 hr,在ASTM #3油中 Shore D, 100 ℃, 70 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏 D,100℃,168 hr,在ASTM #1油中 Shore D, 100°C, 168 hr, in ASTM #1 Oil |
ASTM D471 | ||
邵氏 D,100℃,168 hr,在ASTM #3油中 Shore D, 100 ℃, 168 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏 D,100℃,336 hr,在ASTM #1油中 Shore D, 100 ℃, 336 hr, in ASTM # 1 oil |
ASTM D471 | ||
邵氏 D,100℃,336 hr,在ASTM #3油中 Shore D, 100 ℃, 336 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏 D,100℃,504 hr,在ASTM #1油中 Shore D, 100 ℃, 504 hr, in ASTM # 1 oil |
ASTM D471 | ||
邵氏 D,100℃,504 hr,在ASTM #3油中 Shore D, 100 ℃, 504 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏硬度的变化率 The rate of change in Shore hardness |
ISO 175 | ||
邵氏 D,23℃,70 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 70 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,70 hr,在基准燃料C中 Shore D, 23°C, 70 hr, in Reference Fuel C |
ISO 175 | ||
邵氏 D,23℃,168 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 168 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,168 hr,在基准燃料中 Shore D, 23 ℃, 168 hr, in reference fuel |
ISO 175 | ||
邵氏 D,23℃,336 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 336 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,336 hr,在基准燃料C中 Shore D, 23 ℃, 336 hr, in reference fuel C |
ISO 175 | ||
邵氏 D,23℃,504 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 504 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,504 hr,,在基准燃料C中 Shore D, 23 ℃, 504 hr, in reference fuel C |
ISO 175 | ||
邵氏 D,100℃,70 hr,在ASTM #1油中 Shore D, 100°C, 70 hr, in ASTM #1 Oil |
ISO 175 | ||
邵氏 D,100℃,70 hr,在ASTM #3油中 Shore D, 100 ℃, 70 hr, in ASTM # 3 oil |
ISO 175 | ||
邵氏 D,100℃,168 hr,在ASTM #1油中 Shore D, 100°C, 168 hr, in ASTM #1 Oil |
ISO 175 | ||
邵氏 D,100℃,168 hr,在ASTM #3油中 Shore D, 100 ℃, 168 hr, in ASTM # 3 oil |
ISO 175 | ||
邵氏 D,100℃,336 hr,在ASTM #1油中 Shore D, 100 ℃, 336 hr, in ASTM # 1 oil |
ISO 175 | ||
邵氏 D,100℃,336 hr,在ASTM #3油中 Shore D, 100 ℃, 336 hr, in ASTM # 3 oil |
ISO 175 | ||
邵氏 D,100℃,504 hr,在ASTM #1油中 Shore D, 100 ℃, 504 hr, in ASTM # 1 oil |
ISO 175 | ||
邵氏 D,100℃,504 hr,在ASTM #3油中 Shore D, 100 ℃, 504 hr, in ASTM # 3 oil |
ISO 175 | ||
体积变化 Volume change |
ASTM D471 | ||
23℃,70 hr,in Reference Fuel A 23℃,70 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ASTM D471 | |
23℃,168 hr,in Reference Fuel A 23℃,168 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel A 23℃,336 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel A 23℃,504 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
体积变化 Volume change |
ISO 175 | ||
23℃,70 hr,in Reference Fuel A 23℃,70 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ISO 175 | |
23℃,168 hr,in Reference Fuel A 23℃,168 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel A 23℃,336 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel A 23℃,504 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ISO 175 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
压缩载荷 Compression load |
ASTM D575 | ||
10% 挠曲 10% deflection |
MPa | ASTM D575 | |
15% 挠曲 15% deflection |
MPa | ASTM D575 | |
2% 挠曲 2% deflection |
MPa | ASTM D575 | |
20% 挠曲 20% deflection |
MPa | ASTM D575 | |
25% 挠曲 25% deflection |
MPa | ASTM D575 | |
5% 挠曲 5% deflection |
MPa | ASTM D575 | |
50% 挠曲 50% deflection |
MPa | ASTM D575 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 Post-cured 16 hr at 230°F |
4 速率 A (50°C/h) |
【新闻资讯】查看全部
总投资一百亿美元!埃克森美孚乙烯项目全面启动
2021-11-19 搜料网资讯: 11月16日,总投资约100亿美元的埃克森美孚惠州 乙烯 项目全面启动建设。启动仪式在广东惠州、北京和美国休斯敦三地同时举行。 埃克森美孚公司11月8日对外发布消息称, |
总投资一百亿美元!埃克森美孚乙烯项目全面启动 搜料网资讯:11月16日,总投资约100亿美元的埃克森美孚惠州乙烯项目全面启动建设。启动仪式在广东惠州、北京和美国休斯敦三地同时举行。 埃克森美孚公司11月8日对外发布消息称,公司已作出最终投资决策,全面推进位于广东惠州的化工综合体项目。 据了解,该项目位于惠州大亚湾石化区,项目总投资约100亿美元,整体分两期建设。一期项目包括年产160万吨乙烯的灵活进料蒸汽裂解装置,以及两套年产共计120万吨的高性能线性低密度聚乙烯装置,一套世界最大单体年产50万吨的低密度聚乙烯装置和两套年产共计95万吨的差异化高性能聚丙烯装置,以及重件码头等多个配套工程。计划一期项目竣工投产的同时,启动二期项目建设。 截至目前,项目所涉场地平整已完成,办公中控大楼已建成,重件码头、跨海管廊、地下管网等工程建设稳步推进。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。