牌号简介 About |
---|
EL-337是一种改进的、健康安全的双组分填充、无污染的高温环氧树脂层压系统,专门为室温硬化(B阶段)开发,具有高温特性,适用于高温工具应用。EL-337具有优良的处理性能和织物湿透性,可产生高尺寸稳定性的无空隙工具。EL-337可用于制造大型或小型工具,以及生产零件。EL-337也可与Adtech高温表面涂层ES-219和ES-229一起使用。EL-337制成的工具可在160℃/ 320°F的连续温度下使用,间歇性的温度可达191°C/375°F,而EL-337将在室温下凝胶,必须经过后固化以达到极限强度。系统不包含MDA或VCHD。典型的应用包括:真空成型模具、原型注塑模具、高温粘合夹具、喷涂金属模具、压缩模具、高温叠层模具和用于高温应用的部件。 EL-337 is an improved, health-safe, two component, filled, non-staining, high temp epoxy laminating system specifically developed for room temp hardening (B Stage) with high temp properties for high temp tooling applications. EL-337 has excellent handling properties and fabric wet-out to produce a void free tool with high dimensional stability. EL-337 can be used in the construction of large or small tools, as well as production parts. El-337 can also be used with ADTECH High Temp Surface Coats ES-219 and ES-229. Tools made with EL-337 can be used at continuous temperature of 160°C/320°F, and intermittent temperatures up to 191°C/375°F. While EL-337 will gel at room temp, it must be post-cured to achieve ultimate strength. The system contains no MDA or VCHD. Typical applications include: vacuum form molds, prototype injection molds, high temp bonding fixtures, spray metal molds, compression molds, high temp laminated molds and parts to be used in high temp applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表观密度 Apparent density |
1.26 | g/cm³ | ASTM D1895 |
收缩率 Shrinkage rate |
|||
MD MD |
0.13 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
Cast Bar Cast Bar |
0.598 | J | |
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
25℃ 25℃ |
3000 到 5000 | cP | ASTM D2393 |
脱模时间 stripping time |
|||
25℃ 25℃ |
960 到 1400 | min | |
后固化时间 Post curing time |
hr | ||
工作时间 working hours 4 |
min | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength 2 |
|||
断裂 fracture 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
-- -- 2 |
MPa | ASTM D790 | |
149℃ 149℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ASTM D790 | ||
-- -- 2 |
MPa | ASTM D790 | |
断裂,149℃ Fracture, 149 ℃ |
MPa | ASTM D790 | |
压缩强度 compressive strength 3 |
MPa | ASTM D695 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM E1356 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
贮藏期限 Storage period |
|||
25℃ 25℃ |
wk |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 6 Layer, 10 Ounce Glass Fabric Laminate |
3 Cast Bar |
4 232g |
【新闻资讯】查看全部
液化空气集团与巴斯夫联合“碳捕集”项目获欧盟委员会创新基金支持
2021-11-25 搜料网资讯: 液化空气集团与巴斯夫计划研发全球最大的跨境碳捕集(Carbon Capture and Storage,或 CCS)价值链,以显著减少安特卫普港口产业集群的碳排放。这一名为Kairos@C的联合项目, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |