牌号简介 About |
---|
NYCOA 4112 FR是一种高粘度树脂,特别适用于挤出加工、热成型和吹塑。它的熔融粘度和强度为管子、型材和吹塑制品的加工提供了便利。这种材料专门设计用于要求高硬度、韧性、尺寸稳定性和比标准等级的玻璃纤维增强尼龙6更长的使用寿命的应用。NYCOA 4112 FR可用于紫外线稳定、定制颜色和冲击改良等级。它对油脂、油和其他碳氢化合物也有很好的耐化学性。建议的应用包括发动机罩下的热成型汽车部件和吹塑化学储存罐。 NYCOA 4112 FR is a high viscosity resin particularly suitable for extrusion processing, thermoforming and blow molding. Its melt viscosity and strength provide ease of processing for tubing, profile, and blow molded articles. This material is specifically engineered for applications requiring high stiffness, toughness, dimensional stability, and a greater service life than standard grades of glass reinforced Nylon 6. NYCOA 4112 FR is available in UV stable, custom colors, and impact modified grades. It also has excellent chemical resistance to greases, oils, and other hydrocarbons. Suggested applications include thermoformed under the hood automotive components and blow molded chemical storage reservoirs. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.32 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
ASTM D955 | ||
MD MD |
0.40 | % | ASTM D955 |
TD TD |
0.60 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
1.0 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
6.4mm 6.4mm |
130 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
熔融温度 Melting temperature |
℃ | DSC | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 2 |
MPa | ASTM D790 | |
弯曲强度 bending strength 2 |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
【新闻资讯】查看全部
模具电火花成形加工办法
2016-07-13 模具加工方法是多种多样的,下面我们来分析一下有关电火花成形加工方法知识。电火花成形加工主要是利用在工具和工件(正、负电极)之间产生脉冲性火花放电时的电腐蚀现象来蚀除多余的金属,以达到零件技术要求所规定的尺寸、形状及表面质量。 1、模具电火花成形加工方法必须满足三大条件: ①必须使工具电极和工件被加工表面之间保持一定的间隙,因此在电火花加工中必须具有工具电极的自动进给和调节装置; ②火花放电必须是瞬时的脉冲性放电,为此电火花加工必须使用脉冲电源 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |