牌号简介 About |
---|
V61C是一种氟橡胶(FKM)材料,旨在提高低温应用中的效率和使用寿命。V61C将FKM密封的操作性能比传统FKM等级的操作性能低15°C,并在低温性能方面树立了新的行业基准。V61C具有与传统FKM等级相同的化学和机械性能,可用于几乎任何尺寸的O型环(标准和非标准)和定制设计组件。V61C的主要特点是玻璃化转变温度为-40°C(-40°F),具有最宽的工作温度范围-51°C至+225°C低压缩永久变形,具有优异的密封性能、良好的延伸性能,即使在低温下也更容易安装,具有优异的耐石油、石油、硅酮和双酯液体的典型应用。在冷操作环境中的阀门和泵用于密封暴露在冷环境中的应用,这些应用要求温度的高变化。 V61C is a fluoroelastomer (FKM) material developed to offer increased efficiency and service life in low temperature applications. V61C extends the operational performance of FKM seals by a full 15°C lower than is possible with traditional FKM grades and sets a new industry benchmark in low temperature performance. V61C exhibits the same chemical and mechanical properties as conventional FKM grades and is available in almost any sized O-ring (standard and non -standard) and custom designed components. Key Attributes With a glass transition of -40°C (-40°F), V61C offers the widest operating temperature range of -51°C to +225°C Low compression set giving excellent seal performance Good elongation properties making fitting easier even at low temperature Excellent resistance to petroleum, oil, silicone and di-ester liquids Typical Applications Valves and pumps in cold operating environments Seal applications that are exposed to cold situations Applications that demand high variations in temperature |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
IRHD 硬度 IRHD hardness |
58 | ASTM D1415 , ISO 48 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
10.0 | MPa | ASTM D412 , ISO 37 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
210 | % | ASTM D412,ISO 37 |
压缩形变 Compression deformation |
|||
200℃,24 hr 200℃,24 hr |
18 | % | ASTM D395,ISO 815 |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
|||
250℃,72 hr 250℃,72 hr |
10 | % | ASTM D412 , ISO 37 |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
|||
250℃,72 hr 250℃,72 hr |
% | ASTM D412 , ISO 37 | |
空气中 IRHD 硬度的变化率 The change rate of IRHD hardness in the air |
|||
250℃,72 hr 250℃,72 hr |
ASTM D573 , ISO 188 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | ||
最高工作温度 Maximum operating temperature |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
结合利华敦促行业提速举动,积极应对包装废弃物
2018-01-30 近日,联合利华全球CEO波尔曼呼吁日用消费品行业加大力度,积极应对日益加剧的海洋塑料废弃物挑战,助力实现塑料循环经济。 Ellen MacArthur 基金会的研究发现,每分钟有相当于一装卸卡车载货量的塑料被倒入海洋。预计到2050年,在全球海洋里的塑料重量将多于鱼的重量。目前,全球仅14%的用后塑料包装被收集进入回收环节。 2017年1月,联合利华在业界率先做出承诺,到2025年,实现其产品所用塑料包装100%可再用、可回收或可堆肥。一年后的今天,有10家 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |