牌号简介 About |
---|
YUZEX® 8800提供比具有竞争力的高密度聚乙烯薄膜等级更强的薄膜,该等级是双峰型树脂。因此,YUZEX® 8800在薄膜挤出过程中表现出比同类高密度聚乙烯(HDPE)薄膜树脂优越的稳定性,并使薄膜具有良好的外观。YUZEX® 8800具有超高分子量聚合物,与具有竞争力的高密度聚乙烯薄膜等级相比,具有优异的机械性能。 YUZEX 8800 provides stronger film than ones made from competitive HDPE film grades and this grade is bimodal type resin. Therefore YUZEX 8800 shows superior stability in film extrusion to that of competitive HDPE film resins and gives excellent appearance to its film. YUZEX 8800 has ultra high molecular weight polymer and this make excellent mechanical properties compared with competitive HDPE film grades. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.956 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
0.048 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
> 600 | hr | ASTM D1693 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D638 | ||
屈服 yield |
22.6 | MPa | ASTM D638 |
断裂 fracture |
29.4 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
ASTM D256 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
新型塑料电解质使手机“秒充”
2016-12-20 英国研究人员研发出一种新型塑料电解质替换现有电池,这种新型塑料电解质电容量是目前超级电容器的1000倍,甚至10000倍,这使得手机和电脑“秒充电”有望在两年内成为现实。 与传统意义上的电池不同,超级电容器利用电极和电解质存储能量,充电蓄电相当快速。萨里大学的Brendan Howlin博士表示,全球都在研究新型能量存储技术,这种新型的超容量超级电容器极有可能获得激动人心的进展。 尽管如此,低能量密度是其主要缺陷,超级电容器每公斤存储能量相当低。超级电容器材 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |