牌号简介 About |
---|
这种化合物利用了道康宁开发的聚乙烯交联系统,即所谓的硅橡胶。它是一种三组分系统,包括一种硅基化乙烯聚合物(称为接枝共聚物PP 408)、一种锡基交联催化剂主批次PP 401以及一种主批次P-10040-B(含有润滑剂、紫外线成分和适当等级的炭黑)。这三种材料通常用于90份嫁接,5份催化剂母料和5份特殊黑色母料的比例。这些材料单独存放,相当稳定,但当混合和暴露在水分下时,发生交联。该系统可将该化合物作为普通热塑性塑料挤出,从而在加工过程中获得高水平的交联。成品具有与其他方法交联的聚乙烯有关的所有性能。硅烷接枝黑色交联聚乙烯用于架空电缆。 This compound utilizes the system for cross linking of polyethylene developed by DOW Corning and known as Sioplas. It is a three component system comprising a silylated ethylene polymer known as the graft copolymer PP 408, a tin based cross-linking catalyst master batch PP 401 and also a master batch P-10040-B containing lubricant, UV ingredient and suitable grade of carbon black. These three material are normally used in the ratio of 90 parts graft, 5 parts catalyst master batch and 5 parts special black masterbatches. Stored separately, these materials are fairly stable but when mixed and exposed to moisture, crosslinking takes place. This system allows the compound to be extruded as a normal thermoplastic which will then attain a high level of cross linking in the processed from. The finished product has all the properties associatedwith polyethylene cross linked by other methods. Silane grafted black cross linkable polythylene for over head cables. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.930 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.1 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
19.0 | MPa | IEC 60811 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
550 | % | IEC 60811 |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
|||
135℃,168 hr 135℃,168 hr |
10 | % | IEC 60811 |
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air |
|||
135℃,168 hr 135℃,168 hr |
% | IEC 60811 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固性 thermosetting |
IEC 60811 | ||
伸长率不足 Insufficient elongation |
% | IEC 60811 | |
冷却后最大永久伸长率 Maximum permanent elongation after cooling |
% | IEC 60811 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
20 ℃ 20 ℃ |
ohms·cm | IEC 60502 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
IEC 60250 | ||
功率因数 power factor 1 |
|||
23℃ 23℃ 1 |
IEC 250 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 50 Hz |
【新闻资讯】查看全部
煤炭清洁高效利用仍存三大矛盾
2022-03-19 我国是世界上最大的煤炭生产国和消费国。尽管煤炭在国内一次能源消费中的比重正逐年下降,但在相当长的时间内,其主体能源地位仍不会改变。深刻认识我国能源资源禀赋和煤炭基 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-Polylink Polymer PP 408-401-P-10040-B证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)