牌号简介 About |
---|
AMPLIFY™ TY 1351功能性聚合物是马来酸酐接枝(MAH)聚合物。在软包装的连接层中,AMPLIFY™ TY 1351功能性聚合物促进聚乙烯与阻隔性聚合物(如聚酰胺和其他极性基质)的粘合。主要特点:对聚酰胺有极好的粘附力,优异的物理性能,吹塑和浇铸薄膜的各种工艺和使用温度均符合:美国FDA 21 CFR 175.105欧盟,2011年10月,详细信息请参考相关法规。 AMPLIFY™ TY 1351 Functional Polymer is a maleic anhydride grafted (MAH) polymer. In tie layers for flexible packaging, AMPLIFY TY 1351 Functional Polymer promotes adhesion of Polyethylene to barrier polymers such as polyamide and other polar substrates. Main Characteristics: Excellent adhesion to polyamide Excellent physical properties Wide range of process and service temperature For blown and cast film Complies with: US FDA 21 CFR 175.105 EU, No 10/2011 Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.923 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.1 | g/10min | ASTM D1238,ISO 1133 |
MAH 接枝水平 MAH grafting level 2 |
Low | 内部方法 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
膜耐刺穿性 Membrane puncture resistance |
|||
51 µm 51 µm |
11.6 | J/cm³ | 内部方法 |
割线模量 Secant modulus |
ASTM D882 | ||
2% 正割,MD:51 µm 2% secant, MD: 51 µ m |
209 | MPa | ASTM D882 |
2% 正割,TD:51 µm 2% secant, TD: 51 µ m |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,51 µm MD, yield, 51 µ m |
MPa | ASTM D882 | |
TD,屈服,51 µm TD, yield, 51 µ m |
MPa | ASTM D882 | |
MD,断裂,51 µm MD, fracture, 51 µ m |
MPa | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,51 µm MD, fracture, 51 µ m |
% | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
51 µm 51 µm |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 3 |
ASTM D1922 | ||
MD:51 µm MD:51 µm |
g | ASTM D1922 | |
TD:51 µm TD:51 µm |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.8 µm 45°,50.8 µm |
ASTM D2457 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Low: <0.25 wt%, Medium 0.25-0.5, High >0.5 wt% |
3 Method B |
【新闻资讯】查看全部
新分子或推动可再生塑料“变革”
2021-02-08 搜料网资讯: 随着地球上橡胶和塑料垃圾负担持续增加,科学家们期待能以闭环回收的方式减少垃圾数量。据最新一期《自然化学》杂志报道,美国研究人员发现了一种可能改变游戏规 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |