牌号简介 About |
---|
基于聚酰胺66(PA 66)的化合物。增韧的玻璃纤维。 Polyamide 66 (PA66) based compound. Toughened. Glass fibres. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.30 | g/cm³ | ISO 1183 |
成型收缩率 Molding Shrinkage Molding shrinkage |
ISO 294-4 | ||
TD:2.0 mm TD:2.0 mm |
0.90 to 1.2 | % | ISO 294-4 |
MD:2.0 mm MD:2.0 mm |
0.45 to 0.75 | % | ISO 294-4 |
吸水率 Water Absorption Water Absorption |
|||
23℃,24hr 23℃,24hr |
0.30 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus Tensile Modulus |
ISO 527-2/1 | ||
23℃ 23℃ |
8000 | MPa | ISO 527-1-2 |
60℃ 60℃ |
MPa | ISO 527-1-2 | |
90℃ 90℃ |
MPa | ISO 527-1-2 | |
120℃ 120℃ |
MPa | ISO 527-1-2 | |
150℃ 150℃ |
MPa | ISO 527-1-2 | |
拉伸强度 Tensile Strength Tensile Strength |
ISO 527-2/5 | ||
屈服,60℃ Yield, 60 ℃ |
MPa | ISO 527-2/5 | |
屈服,90℃ Yield, 90 ℃ |
MPa | ISO 527-2/5 | |
屈服,120℃ Yield, 120 ℃ |
MPa | ISO 527-2/5 | |
屈服,150℃ Yield, 150 ℃ |
MPa | ISO 527-2/5 | |
拉伸强度 Tensile Strength Tensile Strength |
ISO 527-2/5 | ||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
断裂,60℃ Fracture, 60 ℃ |
MPa | ISO 527-2/5 | |
断裂,90℃ Fracture, 90 ℃ |
MPa | ISO 527-2/5 | |
断裂,120℃ Fracture, 120 ℃ |
MPa | ISO 527-2/5 | |
断裂,150℃ Fracture, 150 ℃ |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile Strain Tensile Strain |
ISO 527-2/5 | ||
屈服,60℃ Yield, 60 ℃ |
% | ISO 527-2/5 | |
屈服,90℃ Yield, 90 ℃ |
% | ISO 527-2/5 | |
屈服,120℃ Yield, 120 ℃ |
% | ISO 527-2/5 | |
屈服,150℃ Yield, 150 ℃ |
% | ISO 527-2/5 | |
拉伸应变 Tensile Strain Tensile Strain |
ISO 527-2/5 | ||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
断裂,60℃ Fracture, 60 ℃ |
% | ISO 527-2/5 | |
断裂,90℃ Fracture, 90 ℃ |
% | ISO 527-2/5 | |
断裂,120℃ Fracture, 120 ℃ |
% | ISO 527-2/5 | |
断裂,150℃ Fracture, 150 ℃ |
% | ISO 527-2/5 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
ISO 179/1eA | ||
-20℃ -20℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-20℃ -20℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
连续使用温度 Continuous use temperature Continuous use temperature |
℃ | ||
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
|||
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
MD:30~100℃ MD:30~100℃ |
1/℃ | ISO 11359-2 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
尺寸稳定性 dimensional stability |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 at 60 MPa of cavity pressure |
3 20,000 hr |
【新闻资讯】查看全部 ![]()
朗盛、天健龙维 开发塑料变速箱侧盖
2021-12-26 搜料网资讯: 12月13日,朗盛宣布,与汽车零部件制造商河北天健龙维合作,为全球知名SUV、皮卡制造商开发首款由聚酰胺6(PA6)制成的变速箱侧盖。这款塑料侧盖将使注塑成型设计变得更 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |