牌号简介 About |
---|
Pocan T 7141 000000 PET+PBT,40%玻璃纤维/矿物,注塑成型,改善流动性,高热尺寸稳定性 POCAN® T7141 000000 PET+PBT, 40 % glass fibers/mineral, injection molding, improved flowability, high thermal dimension stability POCAN® T7141 000000 PET+PBT, 40 % glass fibers/mineral, injection molding, improved flowability, high thermal dimension stability POCAN® T7141 000000 PET+PBT, 40 % glass fibers/mineral, injection molding, improved flowability, high thermal dimension stability |
产品描述 Product Description
厂家:德国朗盛 LANXESS
类别:PBT+PET PBT+PET
加工条件:注射成型 Injection Molding
性能特点: 尺寸稳定性好; 耐高温; 易流动; Good Dimensional Stability,Good liquidity,High Heat Resistance
填料:玻璃纤维/矿物 40
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.70 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.90 | g/cm³ | ISO 60 |
熔体体积流动速率 Melt Volume Rate |
|||
280℃,2.16 kg 280℃,2.16 kg |
25.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:280℃,2.0 mm TD:280℃,2.0 mm 2 |
0.70 | % | ISO 294-4 |
TD:120℃,2.0 mm,2 hrs TD:120℃,2.0 mm,2 hrs 3 |
0.10 | % | ISO 294-4 |
MD:280℃,2.0 mm MD:280℃,2.0 mm 2 |
% | ISO 294-4 | |
MD:120℃,2.0 mm,2 hrs MD:120℃,2.0 mm,2 hrs 3 |
% | ISO 294-4 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus 4 |
|||
23℃ 23℃ 4 |
MPa | ISO 178-A | |
弯曲强度 bending strength 4 |
|||
23℃ 23℃ 4 |
MPa | ISO 178 | |
弯曲应变 Bending strain 5 |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B120 B120 |
℃ | ISO 306/B120 | |
熔融温度 Melting temperature 5 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.80 mm 0.80 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.8 mm 0.8 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
ISO 7792 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 60x60x2mm, 80°C MT, 600 bar |
3 60x60x2; MT 80°C; 600 Bar |
4 60x60x2 |
5 60x60x2mm |
6 0.079 in/min |
7 2 mm/min |
8 Pull Rate: 2 mm/min; 50% RH |
9 10°C/min |
【新闻资讯】查看全部
聚乙烯市场是否还有转机?
2020-10-29 搜料网资讯: 近日国内聚乙烯市场弱势下行趋势未改。从下表看,上周末至今线性跌幅最大,低压跌幅最小。而从价格看,低压除了部分膜料和拉丝价格偏高外,当前的价格与线性基本 |
聚乙烯市场是否还有转机? 搜料网资讯:近日国内聚乙烯市场弱势下行趋势未改。从下表看,上周末至今线性跌幅最大,低压跌幅最小。而从价格看,低压除了部分膜料和拉丝价格偏高外,当前的价格与线性基本保持同一水平。另外期货震荡走低,更进一步打击业内人士操作心态,尽管当前下游开工率仍有提升,需求良好,但现货市场持续走低也是不争的事实,“金九银十”未能体现。今年的行情仅剩两个月,聚乙烯市场是否还有转机?
从上图我们看到,经过今年上半年恢复性反弹,下半年聚乙烯市场在7000-7500元/吨区间震荡。随着天气转冷,终端需求趋势性转淡,因此当前整体市场出货意愿增强,市场价格有小幅商谈空间。此外据悉部分中东延期货船近期到港,尤其是线性货源,港口库存继续累积,对供应端形成一定压力。而国内供应有增无减,今日万华化学乙烯一体化装置上游裂解装置开车中,下游配套LLDPE装置及低压装置已测试。后期海国龙油石化、延长中煤新增产能释放,自产加进口,社会库存预期增加。 尽管当前下游开工仍受“银十”传统旺季支撑,全国农膜平均开工率在59%左右,但季节性的需求预期转弱。所以在充足的库存保证下,聚乙烯市场走软的概率加大,场内悲观气氛已现端倪。 近日国家统计局数据显示,前三季度全国规模以上工业企业利润同比降幅收窄至2.4%,为今年以来最好水平;9月单月工业企业利润同比增长10.1%,仍保持两位数增长。在国际疫情持续蔓延、国际形势紧张的背景下,我国经济依然向好,塑料的中长期市场可持续看好,但就今年仅剩的短期市场看,聚乙烯市场难有转机,弱势震荡运行或为主基调。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。