牌号简介 About |
---|
NANCAR® 1043是一种中等耐油性的中丙烯腈-丁二烯共聚物。它在低温下聚合,并含有足够的抗氧化剂,以满足正常老化条件。它具有较高的门尼粘度,并提供具有较高强度和模量的化合物。NANCAR® 1043建议用于需要改进低温性能的应用中。南卡1043提供卓越的挤压和一般的加工改进。 NANCAR® 1043 is a medium acrylonitrile butadiene copolymer with medium oil resistance. It is polymerized at low temperature and contains sufficient antioxidant for normal aging conditions. It has high Mooney viscosity and provides compounds with higher strength and modulus. NANCAR® 1043 is recommended for use in applications requiring improved low temperature properties. NANCAR ® 1043 provides excellent extrusion and general processing improvement. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.970 | g/cm³ | |
门尼粘度 Mooney viscosity |
|||
ML 1+4,100℃ ML 1+4,100℃ |
83 | MU | ASTM D1646 |
丙烯腈含量(Bound) Acrylonitrile content (Bound) |
33.0 | % | 内部方法 |
Stabilizer Stabilizer |
Slightly-staining | ||
可溶性 solubility |
|||
in MEK in MEK |
100 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A Shaw's A 2 |
ASTM D2240 | ||
邵氏 A Shaw's A 3 |
ASTM D2240 | ||
邵氏 A Shaw's A 4 |
ASTM D2240 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
300% 应变 300% strain 5 |
MPa | ASTM D412 | |
300% 应变 300% strain 6 |
MPa | ASTM D412 | |
300% 应变 300% strain 7 |
MPa | ASTM D412 | |
拉伸强度 tensile strength |
ASTM D412 | ||
屈服 yield 2 |
MPa | ASTM D412 | |
屈服 yield 3 |
MPa | ASTM D412 | |
屈服 yield 4 |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
ASTM D412 | ||
断裂 fracture 5 |
% | ASTM D412 | |
断裂 fracture 6 |
% | ASTM D412 | |
断裂 fracture 7 |
% | ASTM D412 | |
撕裂强度 tear strength 8 , 3 |
kN/m | ASTM D624 | |
压缩形变 Compression deformation 4 |
|||
100℃,70 hr 100℃,70 hr 4 |
% | ASTM D395 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air 3 |
|||
100℃,70 hr 100℃,70 hr 3 |
% | ASTM D865 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air 3 |
|||
100℃,70 hr 100℃,70 hr 3 |
% | ASTM D865 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air 3 |
|||
邵氏 A,100℃,70 hr Shore A, 100 ℃, 70 hr 3 |
ASTM D865 | ||
拉伸强度的变化率 The rate of change in tensile strength 3 |
ASTM D471 | ||
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
极限伸长率的变化率 Change rate of ultimate elongation 3 |
ASTM D471 | ||
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
邵氏硬度的变化率 The rate of change in Shore hardness 3 |
ASTM D471 | ||
支撐 A,100℃,70 hr,在ASTM #1油中 Support A, 100 ℃, 70 hr, in ASTM # 1 oil |
ASTM D471 | ||
支撐 A,100℃,70 hr,在ASTM #3油中 Support A, 100 ℃, 70 hr, in ASTM # 3 oil |
ASTM D471 | ||
体积变化 Volume change 3 |
ASTM D471 | ||
100℃,70 hr,ASTM 标准油(1号) 100 ℃, 70 hr, ASTM standard oil (No.1) |
% | ASTM D471 | |
100℃,70 hr,ASTM 标准油(3号) 100 ℃, 70 hr, ASTM standard oil (No.3) |
% | ASTM D471 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热损耗 Heat loss |
% | ASTM D5688 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 硫化 20.0 min 在 302°F |
3 硫化 40.0 min 在 302°F |
4 硫化 60.0 min 在 302°F |
5 Cured for 60.0 min at 150°C |
6 Cured for 40.0 min at 150°C |
7 Cured for 20.0 min at 150°C |
8 C 模具 |
【新闻资讯】查看全部
机械手:配合两台注塑机的自动化消费
2018-02-28 威猛机械手:配合两台注塑机的自动化生产 艾福迈汽车系统(上海)有限公司是全德资的汽车零部件制造商,在汽车燃油管理系统、发动机系统、制动系统以及座椅舒适系统方面拥有专业技术。 在生产全新的油箱阀门盖时,由于技术及材料的特殊性,需要使用两台注塑机配合生产。一台注塑机将密封圈注塑成型后,放入另一台注塑机,再注塑阀盖本体。为了解决半成品实时无障碍移转,艾福迈公司管理层在对比了诸多供应商提供的方案后,最终选择了威猛巴顿菲尔作为合作伙伴 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |